牌号简介 About |
---|
ALCUDIA CA-7220B是稳定的与HALS(无色),紫外线吸收剂和抗氧化剂。这些复合薄膜的主要性能是耐太阳辐射、透光性和保温性。用于温室和隧道覆盖的薄膜。200m厚度,1:2:1三层共挤薄膜,中间层为ALCUDIA CA-7421B,外层为ALCUDIA CA-7220B,在最大太阳辐射为160Kly的地理区域具有三年的寿命。如需更多信息,请联系技术援助和发展部或商业关注服务部。由于共挤结构的流变性能不同,各生产线的工艺条件应进行优化。 ALCUDIA® CA-7220B is stabilized with HALS (colourless), UV absorber and antioxidants. The main properties of these compound films are high solar radiation resistance, light transmission and heat retention. APLICATIONS Films for greenhouses and tunnels cover. 200 µm thickness, 1:2:1 three layers coextruded films, with ALCUDIA® CA-7421B in the middle layer and ALCUDIA® CA-7220B in the external layers, have a lifetime of the three years in geographical areas where maximum solar radiation is 160 Kly. For further information, contact to Technical Assistance and Development Department or Commercial Attention Service. Processing conditions should be optimized for each production line because of different rheological properties in coextruded structures. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.928 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.40 | g/10min | ISO 1133 |
丁酯丙烯酸成分 Butyl acrylate composition |
3.0 | wt% | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
200 | µm | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,200 µm,吹塑薄膜 MD, fracture, 200 µ m, blow molded film |
22.0 | MPa | ISO 527-3 |
TD,断裂,200 µm,吹塑薄膜 TD, fracture, 200 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,200 µm,吹塑薄膜 MD, fracture, 200 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,200 µm,吹塑薄膜 TD, fracture, 200 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
200 µm,吹塑薄膜 200 µ m, blow molded film |
g | ISO 7765-1 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ISO 6383-2 | ||
MD:200 µm,吹塑薄膜 MD: 200 µ m, blow molded film |
N | ISO 6383-2 | |
TD:200 µm,吹塑薄膜 TD: 200 µ m, blow molded film |
N | ISO 6383-2 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
200 µm,吹塑薄膜 200 µ m, blow molded film |
% | ASTM D1003 | |
Global Transmission of Visible Light(200.0 µm) Global Transmission of Visible Light(200.0 µm) 2 |
% | EN 13206 | |
IR Absorption(200.0 µm) IR Absorption(200.0 µm) 2 |
% | EN 13206 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Blown Film |
【新闻资讯】查看全部
上海石化管材料经过国度级实验室测试
2017-08-30 日前,新奥燃气使用上海石化低压聚乙烯管材料制成的样品管,通过了国家级实验室1000小时的燃气管道测试。这标志着上海石化高附加值PE管材专用料真正具备完全取代进口原料的能力,可广泛应用于燃气管道领域。 此前,国内PE燃气管材专用料主要依赖进口,以北欧化工、英力士、道达尔、SABIC等欧洲和中东料为主。近年来,虽然国内石化企业加快了PE燃气管材专用料的研究和开发步伐,并取得一定进展,但能满足燃气管材专用料要求的生产厂家相对较少,不仅专用料牌号少,而且质量性能不够稳定。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |