Elix Ultra HH 4115 PG超高耐热ABS电镀等级ISO shortname:ISO 2580-1 ABS 2-X,MG,115-15-35-20主要优点是具有极强的抗冲击性,低温延展性非常高,冲击温度高达-30°C,流动性、耐热性和柔韧性良好,在注塑过程中排放和气味等级较低的模具沉积物。加工应用尺寸精度好,收缩率低,CLTE。密度低于PC/ABS化学成分聚碳酸酯改性丙烯腈-丁二烯-苯乙烯共聚物 ELIX ULTRA HH 4115 PG Very high heat resistance ABS plating grade ISO shortname: ISO 2580-1 ABS 2-X, MG, 115-15-35-20 Major Benefits Extreme impact resistance with low temperature ductility Very high impact up to -30°C Well balanced flowability, heat resistance and flexibility Low emission and odor grade Lower mould deposits in injection molding processing applications Good dimensional precision, low shrinkage and CLTE. Lower density than PC/ABS Chemical composition Acrylonitrile-butadiene-styrene (ABS) copolymer modified with polycarbonate and poly(styrene-co-maleimide) |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
25℃ 25℃ |
1.07 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
3.0 | g/10min | ASTM D1238 |
熔体体积流动速率 Melt Volume Rate |
|||
260℃,5 kg 260℃,5 kg |
14.0 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate 2 |
|||
TD TD |
0.65 到 0.75 | % | |
MD MD |
0.65 到 0.75 | % | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃,3.2mm -30℃,3.2mm |
J/m | ASTM D256 | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ISO 75-2/B | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
-- -- |
℃ | ASTM D1525 6 | |
B120 B120 |
℃ | ISO 306/B120 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
燃烧速率 Burning rate 7 |
|||
2.0 mm 2.0 mm 7 |
mm/min | ISO 3795 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
球压硬度 Ball hardness |
MPa | ISO 2039-1 | |
拉伸模量 Tensile modulus |
|||
-- -- 3 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
-- -- 4 |
MPa | ASTM D790 | |
-- -- 5 |
MPa | ISO 178 | |
弯曲强度 bending strength 5 |
MPa | ISO 178 |
备注 |
---|
2、60x60x2 mm |
3、5.0 mm/min |
4、1.3 mm/min |
5、2.0 mm/min |
6、速率 A (50°C/h), 载荷2 (50N) |
7、US-FMVSS |
【新闻资讯】查看全部
朗盛一季度销售额增长近7%,约26亿欧元
2018-05-09 朗盛一季度销售额增长近7%,约26亿欧元 消极货币影响下仍达到最佳季度业绩 常规业务范围内息税折旧及摊销前利润(EBITDA)增长14%,达3.75亿欧元 常规业务范围内息税折旧及摊销前利润(EBITDA)率14.6% 净利润提高23%,达9600万欧元 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |