牌号简介 About |
---|
符合ISO 1043-1的材料规范:用40%重量%长的玻璃纤维增强的PP紫外线稳定聚丙烯,低排放。纤维与聚丙烯基体发生化学耦合。球是圆柱形的,通常也包括10 mm长的嵌入纤维。Celstran成型件具有高强度、高刚度、高热变形等优异的力学性能。由于部件中内置了纤维骨架,因此在高温和低温下缺口冲击强度会增加。长纤维增强能显著降低蠕变。模制品的各向同性收缩使翘曲最小化。通过注射成型,可以制造出具有高再现性的复杂零件。应用领域:汽车功能/结构件 Material code according to ISO 1043-1: PP UV-stabilized polypropylene reinforced with 40 weight percent long glass fibers, low emission. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long. Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly. The very isotropic shrinkage in the molded parts minimizes the warpage. Complex parts can be manufactured with high reproducibility by injection molding. Application field: Functional/structural parts for automotive |
产品描述 Product Description
厂家:美国塞拉尼斯 Celanese
类别:PP PP not specified
用途:汽车领域的应用;
加工条件:注射成型 Injection Molding
性能特点: 机械强度好; 化学耦合; 低VOC; 耐低温冲击; 各向同性好; 低翘曲性; 耐候抗UV; 韧性好; Good Rigidity,Weather resistance is good,Low warping,Good flexibility,Low odor,Chemical coupling,low-temperature impact resistance,Good Isotropy
紫外线:UV Stabilized
填料:玻璃纤维 40
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.22 | g/cm³ | ISO 1183 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
9200 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
断裂 fracture |
130 | MPa | ISO 527-2/1A/5 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.0 | % | ISO 527-2/1A/5 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
9000 | MPa | |
80℃ 80℃ |
MPa | ||
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ||
80℃ 80℃ |
MPa | ||
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
-30℃ -30℃ |
kJ/m² | ||
23℃ 23℃ |
kJ/m² | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 |
备注 |
---|
2. 10°C/min |
【新闻资讯】查看全部
上海质监局公布2016年保鲜膜抽查结果
2016-03-09 从上海市质量技术监督局官网获悉,近期,该局组织相关质检机构对上海市生产的保鲜膜进行了专项监督抽查,共计抽查产品12批次,经检验,不合格0批次。 本次抽查依据GB 10457《聚乙烯自粘保鲜膜》、GB 9687《 食品包装用聚乙烯成型品卫生标准》等国家标准及相关标准要求,对保鲜膜的下列项目进行了检验:拉伸强度、气体透过率(氧)、、水蒸气透过量、自粘性、感官、蒸发残渣、高锰酸钾消耗量、重金属(以Pb计)、脱色试验等。 |
上海质监局公布2016年保鲜膜抽查结果 从上海质监局官方网站获知,最近,各地各部门机构有关质量检验组织对上海生产制造的保鲜膜开展了重点监管抽查,总共抽查商品12批号,经检测,不过关0批号。 此次抽查根据GB 10457《聚乙烯自粘保鲜膜》、GB 9687《 食品包装用聚乙烯成型品卫生标准》等国家行业标准及有关规范规定,对保鲜膜的下述新项目开展了检测:抗拉强度、汽体透过率(氧)、、水蒸汽通过量、自粘性、感观、蒸发残渣、高锰酸钾溶液使用量、重金属超标(以Pb计)、褪色实验等。 来源于:中国质量检验报刊社 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。