牌号简介 About |
---|
SACO高分子PFP026M-13是一种天然无卤阻燃RoHS聚烯烃化合物。它设计用于各种各样的挤压应用。该化合物具有优良的防火性能,包括火焰传播慢、自熄性好、发烟量小。SACO高分子PFP026M-13应采用螺杆结构挤压,以优化工艺条件和生产能力。 SACO-Macromeric ® PFP026M-13 is a natural, non-halogen flame retardant RoHS polyolefin compound. It is designed for use in a wide variety extrusion applications. This compound has superior fire performance; including slow flame propagation, self-extinguishing characteristics, and low smoke production. SACO-Macromeric ® PFP026M-13 should be extruded with a screw configuration designed to optimize process conditions and throughput. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density 2 |
1.55 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,5.0kg 230℃,5.0kg |
3.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂 fracture |
13.4 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
40 | % | ASTM D638 |
弯曲模量 Bending modulus |
|||
1% 正割 1% secant |
1210 | MPa | ASTM D790 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-5℃ -5℃ |
J/m | ASTM D256 | |
落锤冲击 Drop hammer impact 3 , 4 |
J | ASTM D5420 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.60 mm 1.60 mm |
|||
3.20 mm 3.20 mm |
备注 |
---|
2. 23°C |
3. 几何形状GB |
4. 8-lbs |
【新闻资讯】查看全部
巴斯夫:汽车内饰聚氨酯组合料发泡模仿技术
2016-09-09 巴斯夫日前推出了一项针对汽车内饰聚氨酯组合料的新服务:升级版巴斯夫Ultrasim® 模拟工具现在已经能够精确模拟开模与合模的聚氨酯组合料发泡过程。从采用Elastoflex® E 半硬质组合料制造的仪表板来看,这项服务极为成功。国际汽车供应商延锋汽车饰件系统采用这一虚拟工艺设计技术开发宝马X1等车型的仪表板。巴斯夫根据每个仪表盘的计算机辅助工程(CAE)模型以及Ultrasim® 中关于半硬质组合料的材料描述,开发了一种发泡模拟技术,使客户能够在实际开发模具之前便发现部件可能存在的设计和 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |