牌号简介 About |
---|
CC7209是专为密封剥离应用而设计的挤压涂层等级。当密封在自身和PE上时,它能产生光滑和容易的剥离。CC7209还可以很好地粘附到各种基底上,尤其是铝。本发明的方法是将其与比例为1:1的标准低密度聚乙烯(LDPE)进行混合处理,如使用标准低密度聚乙烯(LDPE)。材料必须预先干燥,但仍有轻微的堵塞过滤器和填料结块的风险。CC7209含有30%的细分散填料。CC7209包含细分散填料,但不含其他添加剂。 CC7209 is an extrusion coating grade especially designed for seal-peel applications. It gives smooth and easy peel when sealed against itself and PE. CC7209 provides also good adhesion to various substrates, particularly to aluminium. The rocommendation is to mix it with standard LDPE with the ratio 1:1 In this mixture processing like standard LDPE can be applied. The material must be pre-dried but there can be still a slight risk for filter blocking and filler agglomeration. CC7209 contains 30 percent finely dispersed filler CAS-No.: 9002-88-4 Applications CC7209 is recommended for: extrusion coated seal-peel structures Food packaging tie layer for aluminium in extrusion coated/laminated structures Additives CC7209 contains finely dispersed filler but no other additives. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.15 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
5.2 | g/10min | ISO 1133 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
怎样处理塑料制品加工中的气泡成绩
2015-12-10 气泡常常发生在塑料制品最后接缝处或制品较厚的部分。制品在模型内首先是表面冷却,当外表面已冷却,中心部分仍处于热的状态。中心部分冷却时要收缩,而塑料表面已经冷却,因此只能由内部自己收缩而形成气泡。有许多厚的制件在出模时还没有气泡,但是经过数十秒钟后,在中心部分就有气泡出现。 气泡有几种情况,现象不同,原因也不同,分述如下: (1)较厚的制品,表面发胖而鼓 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |