牌号简介 About |
---|
Amodel AS -1133 HS是33%玻纤增强热稳定型聚邻苯二甲酰胺(PPA)树脂,即使是那些壁厚大于0.125英寸( 3毫米)的成型部件,也具有优异的结构完整性 。 该结构性树脂的主要特性包括高热变形温度、高挠曲模量、高拉伸强度、优良的耐蠕变性和低吸湿性。 -黑色: AS-1145 HS BK 324 -本色: AS-1145 HS NT Amodel® AS-1145 HS is a 45% glass reinforced heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts, even those with wall thicknesses greater than 0.125 inch (3 mm). Key properties of this structural resin are high heat deflection temperature, high flexural modulus, high tensile strength, excellent creep resistance, and low moisture absorption. Black: AS-1145 HS BK 324 Natural: AS-1145 HS NT |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.56 | g/cm³ | ISO 1183/A |
收缩率 Shrinkage rate |
|||
TD TD |
0.60 | % | ASTM D955 |
MD MD |
0.20 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
0.12 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
12 | kJ/m² | ISO 179-1eA |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
kJ/m² | ISO 180-1A | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,3.18 mm 1.8 MPa, annealed, 3.18 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,退火,3.2 mm 0.45 MPa, annealed, 3.2 mm |
℃ | ASTM D648 | |
连续使用温度 Continuous use temperature |
ASTM D3045 | ||
-- -- 2 |
℃ | ASTM D3045 | |
-- -- 3 |
℃ | ASTM D3045 | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3418 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
160 到 249℃ 160 to 249 ℃ |
cm/cm/℃ | ASTM E831 | |
MD MD |
ASTM E831 | ||
0 到 100℃ 0 to 100 ℃ |
cm/cm/℃ | ASTM E831 | |
160 到 249℃ 160 to 249 ℃ |
cm/cm/℃ | ASTM E831 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耐电弧性 Arc resistance |
sec | ASTM D495 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 4 |
|||
3.20 mm 3.20 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
屈服 yield |
MPa | ASTM D790 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
泊松比 Poisson's ratio |
ASTM E132 | ||
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 20000小时 |
3 5000小时 |
4 这些可燃性等级不代表这些材料或任何其他材料在实际着火灾情况下的危险性。 |
【新闻资讯】查看全部
新进展!青州天安化工12万吨/年PBAT项目公示
2021-06-15 搜料网资讯: 6月9日,天安化工 12万吨/年 PBAT 可 完全生物降解聚酯项目建设用地规划许可批前公示。 项目概况 建设项目名称:天安化工12万吨/年PBAT可完全生物降解聚酯项目 建设单位 |
新进展!青州天安化工12万吨/年PBAT项目公示 搜料网资讯:6月9日,天安化工12万吨/年PBAT可完全生物降解聚酯项目建设用地规划许可批前公示。 项目概况 建设项目名称:天安化工12万吨/年PBAT可完全生物降解聚酯项目 建设单位:青州天安化工有限公司 建设位置:昭德路与龙华街交叉口东北侧 用地面积:59141平方米 用地性质:工业用地 审批依据:《中华人民共和国城乡规划法》、《山东省城乡规划条例》 公示时间:2021年6月9日——2021年6月16日 项目规划图 青州天安化工有限公司,成立于2007年10月。现公司拥有20万吨/年碳四改质装置、50万吨/年碳四丁烯异构装置、40万吨/年萃取装置、30万吨/年MTBE及配套装置各一套。主要生产MTBE、异构油、轻烃、重烃和优质液化气等。所需原料为醚后碳四,高烯烃碳四,甲醇,石脑油。 响应国家的禁塑令。2020年11月30日,青州天安化工有限公司与中国纺织科学研究院聚友化工,在山东省青州市经济开发区高分子化工园区,规划建设年产20万吨/年PBS/PBAT可完全生物降解高分子聚酯项目。 项目概况 项目名称:20万吨/年PBAT/PBS可完全生物降解聚酯装置项目。 项目建设内容:该项目分二期进行;一期3万吨/年丁二酸5万吨/年PBAT/PBS可完全生物降聚酯项目,计划在2020年12月份对长周期制作设备开始招标,2021年2月份土建施工建设。二期15万吨/年生产线计划在2022年3月份土建施工建设。 该项目可根据市场需求灵活生产PBAT、PBS可完全生物降解聚酯产品,同时具备扩链改性生产其它不同牌号产品的能力。该项目主要建设酯化、聚合单元、制冷单元、热媒站单元、四氢呋喃单元、原料和成品储运设施及公用工程。 项目投资金额:一期投资总金额5.8亿元,二期投资15亿元。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。