牌号简介 About |
---|
Vydyne® 41H NT是通用的冲击改性PA66树脂。天然的,它是热稳定的,以提高抵抗高温。Vydyne® 41H NT的热稳定包装是为了在预期持续或延长高温暴露的应用中使用时提供热耐久性而制定的。Vydyne® 41H NT是公认的所有加工和性能优势固有的PA66与提高冲击强度。该树脂具有高熔点、良好的表面润滑性、耐磨性和对许多化学品、机器和汽车油、溶剂和汽油的抵抗力等工程性能的良好平衡组合。 Vydyne 41H NT is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 41H NT was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated. Vydyne 41H NT is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:2.0 mm TD:2.0 mm |
1.6 | % | ISO 294-4 |
MD:2.0 mm MD:2.0 mm |
1.8 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
2.1 | % | ISO 62 |
23℃,24hr 23℃,24hr |
1.0 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2 | |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-40℃ -40℃ |
kJ/m² | ISO 179 | |
-30℃ -30℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-30℃ -30℃ |
ISO 179 | ||
23℃ 23℃ |
ISO 179 | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180 | ||
-40℃ -40℃ |
kJ/m² | ISO 180 | |
-30℃ -30℃ |
kJ/m² | ISO 180 | |
23℃ 23℃ |
kJ/m² | ISO 180 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃,2 mm TD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
MD:23~55℃,2 mm MD:23~55℃,2 mm |
1/℃ | ISO 11359-2 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
UL 746 | ||
0.75 mm 0.75 mm |
℃ | UL 746 | |
1.5 mm 1.5 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
|||
0.75 mm 0.75 mm |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
1 mm 1 mm |
kV/mm | IEC 60243 | |
耐电弧性 Arc resistance |
|||
3.0 mm 3.0 mm |
ASTM D495 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
3.00 mm 3.00 mm |
V | IEC 60112 | |
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
高电压电弧起痕速率 High voltage arc marking rate |
|||
HVTR HVTR |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
0.75 mm 0.75 mm |
UL 746 | ||
1.5 mm 1.5 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.75 mm 0.75 mm |
UL 94 | ||
1.50 mm 1.50 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
IEC 60695-2-12 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-12 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-12 | |
3.0 mm 3.0 mm |
℃ | IEC 60695-2-12 | |
灼热丝起燃温度 Igniting temperature of the hot wire |
IEC 60695-2-13 | ||
0.75 mm 0.75 mm |
℃ | IEC 60695-2-13 | |
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
3 mm 3 mm |
℃ | IEC 60695-2-13 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
汽车材料 Automotive materials |
|||
thickness d = 1 mm thickness d = 1 mm |
FMVSS 302 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
中央环保例查分两批开展
2019-02-28 据悉,从2019年开始,用三年左右的时间完成第二轮中央生态环境保护例行督察,再用一年时间完成第二轮督察“回头看”。第二轮督察将适当扩展督察范围,把国务院有关部门和央企纳入督察对象。 在生态环境部当天举行的发布会上,中央生态环境保护督察办公室常务副主任介绍,第一轮督察实现31个省(区、市)全覆盖,2018年5月和10月,分两批对全国20个省(区)开展“回头看”。通过“群众举报”、“责令整改”、“立案处罚”“罚款”、“立案侦查”、“行政和刑事拘留”“约谈”、“问责”等方式,截至 |
中央环保例查分两批开展 据悉,从2019年开始,用三年左右的时间完成第二轮中央生态环境保护例行督察,再用一年时间完成第二轮督察“回头看”。第二轮督察将适当扩展督察范围,把国务院有关部门和央企纳入督察对象。 在生态环境部当天举行的发布会上,中央生态环境保护督察办公室常务副主任介绍,第一轮督察实现31个省(区、市)全覆盖,2018年5月和10月,分两批对全国20个省(区)开展“回头看”。通过“群众举报”、“责令整改”、“立案处罚”“罚款”、“立案侦查”、“行政和刑事拘留”“约谈”、“问责”等方式,截至12月20日,直接推动解决群众身边生态环境问题7万余件。 第二轮督察要适当扩展督察范围,将国务院有关部门和承担生态环保任务较重的央企纳入督察对象;将继续探索创新督察方法,加大卫星遥感、红外识别、无人机、大数据等技术应用;将紧盯督察整改落实,针对重点问题咬住不放,不彻底解决绝不松手。 推动生态环境保护督察向纵深发展,还要针对重点区域、重点领域、重点行业突出生态环境问题,组织开展专项督察。专项督察有三个重点,分别是污染防治攻坚战7大标志性战役及其他重点领域;督察整改不力,特别是敷衍整改、表面整改、假装整改等突出问题;人民群众反映突出的生态环境问题。 环保的双面性: 近两年的环保监管检查对电石行业的影响举足轻重,电石行业自身环保问题、追溯到下游PVC行业受此影响实际产出受到明显限制。首先我们来看一下环保政策对PVC企业的影响,环保高压下PVC 企业减产、停产时有发生。有的PVC企业减产,有所停产半个月甚至更长时间,有的被吊销营业执照,典型案例就是新疆宜化停车自2017年停车至2018年年底,但目前来看,PVC整体开工率较高,维持在86%左右。 其次,近年来在环保压力下,2013-2015年PVC产能均为负增长。但是在环保风暴下,也同时淘汰了落后产能,关掉“僵尸企业”,提升了行业的集中度与竞争力,企业开工率大幅提高,产量也明显增加。 环保对于原料电石的影响 众所周知,中国是世界上最大的PVC生产国和消费国,但由于我国“富煤、贫油、少气”的能源结构特点,使得“煤炭―电石―乙炔―有机合成”的煤化工工艺路线成为中国产PVC的主要途径。据统计表明,目前电石法PVC约占总产能的80%多。大部分电石企业通常将其部分回收作为低附加值的水泥原料或石灰原料,甚至直接将其进行露天堆放、晾晒或填埋,不仅占用大量土地、增加企业处置成本,还会造成附近土壤、水体和空气污染,成为限制行业发展和阻碍生态环境保护的重要因素。通过近两年的环保检查,使得电石供应趋于紧张,涨价也较为频繁。通过环保检修等措施,淘汰了“脏、乱、差”的等污染严重的小型电石企业,同时,电石市场下游产品单一,也导致了电石过度依赖下游PVC市场的走向。通过环保等方式淘汰落后产能,能够推动下游消费多元化,有利于节能减排。 2013-2018 年华东地区PVC电石法价格走势图 综上,当前,宏观面无利好消息支撑,上游电石价格疲软,短期来看,PVC难有涨价的可能,预计各地价格窄幅整理,不乏下跌的可能。中长期来看,在需求乏力的情况下,行情难有调涨,预计各地市场将小幅下探。 来源:中宇资讯 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
- 汽车卡扣
- 2019-03-18 159
- Vydyne® 21SPF是一种通用的PA66树脂。它是天然的,主要设计用于注塑加工,树脂允许生产具有良好初始颜色和良好性能
- 阅读全文
汽车卡扣
2-Vydyne® 21SPF树脂允许生产具有良好初始颜色和良好性能和使用再研磨时保持颜色的成型零件
4-树脂经保险商实验室认可,符合许多工业、联邦和军用优质通用PA66树脂规范的要求
- 汽车碳罐
- 2019-03-18 84
- Vydyne® 47H NT是通用的冲击改性PA66树脂,热稳定包装是为了在预期持续或延长高温暴露的应用中使用时提供热耐久性而制定的
- 阅读全文
汽车碳罐
2-Vydyne® 47H NT的热稳定包装是为了在预期持续或延长高温暴露的应用中使用时提供热耐久性而制定的
抱歉!暂无数据。