牌号简介 About |
---|
Starflam RF0068E是一种用于注塑应用的玻璃纤维增强阻燃剂PA66。该材料不含卤素和红磷。 |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Density Density |
1.43 | g/cm³ | ISO 1183 |
Water Absorption Water Absorption |
ISO 62 | ||
23°C, 24 hr 23°C, 24 hr |
0.8 | % | ISO 62 |
Equilibrium, 23°C, 50% RH Equilibrium, 23°C, 50% RH |
0.9 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Tensile Modulus (23°C) Tensile Modulus (23°C) |
10686.9 | mpa | ISO 527-2 |
Tensile Stress (Break, 23°C) Tensile Stress (Break, 23°C) |
133.1 | mpa | ISO 527-2 |
Tensile Strain (Break, 23°C) Tensile Strain (Break, 23°C) |
% | ISO 527-2 | |
Flexural Modulus (23°C) Flexural Modulus (23°C) |
mpa | ISO 178 | |
Flexural Strength (23°C) Flexural Strength (23°C) |
mpa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Charpy Notched Impact Strength Charpy Notched Impact Strength |
ISO 179/1eA | ||
+23°C +23°C |
ftlb/in² | ISO 179/1eA | |
-30°C -30°C |
ftlb/in² | ISO 179/1eA | |
-40°C -40°C |
ftlb/in² | ISO 179/1eA | |
Charpy Unnotched Impact Strength Charpy Unnotched Impact Strength |
ISO 179/1eU | ||
+23°C +23°C |
ftlb/in² | ISO 179/1eU | |
-30°C -30°C |
ftlb/in² | ISO 179/1eU | |
-40°C -40°C |
ftlb/in² | ISO 179/1eU | |
Notched Izod Impact Strength Notched Izod Impact Strength |
ISO 180/1A | ||
+23°C +23°C |
ftlb/in² | ISO 180/1A | |
-30°C -30°C |
ftlb/in² | ISO 180/1A | |
-40°C -40°C |
ftlb/in² | ISO 180/1A | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Heat Deflection Temperature Heat Deflection Temperature |
ISO 75-2/A | ||
1.80 MPa, Unannealed 1.80 MPa, Unannealed |
℃ | ISO 75-2/A | |
0.45 MPa, Unannealed 0.45 MPa, Unannealed |
℃ | ISO 75-2/B | |
Melting Temperature Melting Temperature |
℃ | ISO 11357-3 | |
RTI Elec RTI Elec |
UL 746 | ||
0.750 mm 0.750 mm |
℃ | UL 746 | |
3.00 mm 3.00 mm |
℃ | UL 746 | |
RTI Imp RTI Imp |
UL 746 | ||
0.750 mm 0.750 mm |
℃ | UL 746 | |
3.00 mm 3.00 mm |
℃ | UL 746 | |
RTI Str RTI Str |
UL 746 | ||
0.750 mm 0.750 mm |
℃ | UL 746 | |
3.00 mm 3.00 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Dielectric Strength (1.00 mm) Dielectric Strength (1.00 mm) |
kV/in | IEC 60243 | |
Comparative Tracking Index (3.00 mm) Comparative Tracking Index (3.00 mm) |
V | IEC 60112 | |
High Amp Arc Ignition (HAI) High Amp Arc Ignition (HAI) |
UL 746 | ||
0.750 mm 0.750 mm |
- | UL 746 | |
3.00 mm 3.00 mm |
- | UL 746 | |
Hot-wire Ignition (HWI) Hot-wire Ignition (HWI) |
UL 746 | ||
0.750 mm 0.750 mm |
- | UL 746 | |
3.00 mm 3.00 mm |
- | UL 746 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
2018这四大机遇,各位塑料同胞能抓住吗?
2018-01-15 2017年对于塑料化工行业,可谓是喜忧参半,一方面机械制造的喜人业绩是全球市场份额的屡创新高,新材料工艺不断的提高完善及全球原材料销售井喷;另一方面,全球各大环保组织对 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |