牌号简介 About |
---|
Texin® 288是一种芳香族聚酯基热塑性聚氨酯,硬度约为88A,可通过注塑加工。挤出工艺也可用于某些应用。 Texin 288 is an aromatic polyester-based thermoplastic polyurethane with a hardness of approximately 88A. It can be processed by injection molding. Extrusion processes are also possible for some applications. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 |
密度 Density |
1.20 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:2.54 mm TD:2.54 mm |
0.80 | % | ASTM D955 |
MD:2.54 mm MD:2.54 mm |
0.80 | % | ASTM D955 |
TD:2.54 mm TD:2.54 mm |
0.80 | % | ISO 2577 |
MD:2.54 mm MD:2.54 mm |
% | ISO 2577 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A |
ASTM D2240 | ||
邵氏 D Shaw's D |
ASTM D2240 | ||
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 A Shaw's A |
ISO 868 | ||
邵氏 D Shaw's D |
ISO 868 | ||
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ISO 4649 | |
1000 周期,1000 g,H-18 转轮 1000 cycles, 1000 g, H-18 wheels |
mg | ASTM D1044 | |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 37 | |
屈服 yield |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ASTM D412 | |
300% 应变 300% strain |
MPa | ISO 37 | |
100% 应变 100% strain |
MPa | ASTM D412 | |
100% 应变 100% strain |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ISO 37 | |
断裂 fracture |
% | ASTM D412 | |
撕裂强度 tear strength 2 |
kN/m | ASTM D624 | |
撕裂强度 tear strength |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
|||
23℃,22 hr 23℃,22 hr |
% | ASTM D395 | |
23℃,22 hr 23℃,22 hr 3 |
% | ASTM D395B | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr 3 |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
23℃,22 hr 23℃,22 hr 3 |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr 3 |
% | ISO 815 | |
巴肖氏弹性 Basho's elasticity |
% | ASTM D2632 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
℃ | DMA | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
A50 A50 |
℃ | ISO 306/A50 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 Post-cured 16 hr at 230°F |
4 速率 A (50°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
巴斯夫、三井化学联手促进化学回收
2021-06-02 搜料网资讯: 巴斯夫和三井化学在6月1号的一份联合声明中说,他们已经开始了一项合作研究,以促进日本的化学回收。 声明中称:巴斯夫和三井化学将评估合作的商业模式和各种选择 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |