牌号简介 About |
---|
Hifax 7430 XEP是一种反应器TPO(热塑性聚烯烃),采用Lyondellbasell专有的Catalloy工艺技术制造。它是一种高熔体流动、中高弯曲模量、高结晶度的共聚物,具有良好的冲击和刚度平衡。它主要用于需要低温高速冲击性能的内饰应用。它也被用作汽车和工业应用的复合材料中的一种成分。该等级为天然颗粒形式。有关法规遵从性信息,请参阅Hifax 7430 XEP产品管理公告(PSB)。 Hifax 7430 XEP is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is a high melt flow, medium-high flexural modulus, highly crystalline copolymer with good balance of impact and stiffness. It is primarily used in interior trim applications requiring low temperature high speed impact performance. It is also used as a component in compounded materials for automotive and industrial applications. The grade is available in natural pellet form. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.890 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
19 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,15 秒 Shore D, 15 seconds |
56 | ISO 868 | |
邵氏 D,15 秒 Shore D, 15 seconds |
56 | ASTM D2240 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
14.0 | MPa | ISO 527-2/50 |
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/50 | |
屈服,23℃ Yield, 23 ℃ |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus 2 |
|||
弦,23℃ String, 23 ℃ 2 |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-40℃,完全断裂 -40 ℃, completely fractured |
kJ/m² | ISO 180-1A | |
23℃,完全断裂 23 ℃, completely fractured |
kJ/m² | ISO 180-1A | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 3 |
ASTM D3763 | ||
-40℃,3.20 mm,Total Energy,Ductile Failure -40℃,3.20 mm,Total Energy,Ductile Failure |
J | ASTM D3763 | |
23℃,3.20 mm,Peak Energy,Ductile Failure 23℃,3.20 mm,Peak Energy,Ductile Failure |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 0.079 in/min |
3 7.22 ft/sec |
【新闻资讯】查看全部
黄山邮政管理局联合多部门开展全市塑料污染治理专项行动
2021-01-30 搜料网资讯: 为贯彻落实党中央、国务院关于加强塑料污染治理的决策部署,推进塑料治理方案落实,近日,黄山市邮政管理局联合市发改、住建、文旅局等部门开展全市塑料污染治理 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |