牌号简介 About |
---|
Styrolution PS 158N/L是耐热、速冻通用等级。它适用于膨胀片材和薄膜;在热接触应用中与高冲击聚苯乙烯混合;在与苯乙烯混合的透明、抗冲击应用中。具有高耐热性,成型过程中快速冻结,UL 94 HB(仅限安特卫普)应用,XPS医疗实验室软件与HIPS混合,提高热稳定性。 Styrolution PS 158N/L is a heat resistant, rapid freezing general purpose grade. It is suitable for expanded sheet and film; for blends with high impact polystyrene in heat contact applications; for transparent, impact resistant applications in blends with Styrolux. FEATURES High heat resistance Rapid freezing during molding UL 94 HB (Antwerp only) APPLICATIONS XPS Medical labware Blends with HIPS for increased heat stability |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体体积流动速率 Melt Volume Rate |
|||
200℃,5 kg 200℃,5 kg |
3.30 | cm³/10min | ISO 1133 |
收缩率 Shrinkage rate |
0.30 to 0.60 | % | ISO 294-4 |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
< 0.10 | % | ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
< 0.10 | % | ISO 62 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 2 |
|||
1.8 MPa,退火 1.8 MPa, annealed 2 |
℃ | ISO 75-2/A | |
0.45 MPa,退火 0.45 MPa, annealed 2 |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 3 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ISO 11359-2 | |
导热系数 Thermal conductivity coefficient |
W/m/K | DIN 52612 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电常数 Dielectric constant |
|||
100 Hz 100 Hz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level 5 |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
MPa | ISO 899-1 | |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
MPa | ISO 899-1 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 4h/80°C |
3 标准 B (120°C/h), 压 力1 (10N) |
4 Antwerp Only |
【新闻资讯】查看全部
原油再度破百,日内涨超7%!OPEC+提高增产目标无望
2022-02-28 智通财经APP获悉,周一,布伦特原油亚盘开涨超5%,报103.89美元/桶;WTI原油再度涨破100美元/桶,日内涨超7%。至少10家俄罗斯石油贸易商预计从周一开始将出现大规模出口中断。而OPEC似 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |