牌号简介 About |
---|
SABIC® LLDPE 6218BE是一种用于浇铸薄膜的己烯线性低密度聚乙烯树脂。该产品经过特殊配方设计,在高温下具有最佳的热稳定性,用于铸膜挤出。SABIC® LLDPE 6218BE铸膜具有良好的光学性能、韧性、抗穿刺性和撕裂强度。后缀e表示欧洲血统。应用SABIC® LLDPE 6218BE树脂通常用于托盘拉伸包装(预拉伸)、高性能拉伸膜和其他单层和共挤膜应用,需要高强度。为提高强度,建议与乙烯/丁烯共聚物LLDPE和LDPE共混。本产品不适用于任何医药/医疗应用,也不得用于任何医药/医疗应用。 SABIC® LLDPE 6218BE is a hexene linear low density polyethylene resin for cast film applications. The product has been specially formulated for optimum thermal stability at high temperatures used in cast film extrusion. Cast films produced from SABIC® LLDPE 6218BE exhibit good optical properties, improved toughness, puncture resistance and tear strength. The suffix E denotes European origin. Application SABIC® LLDPE 6218BE resin is typcially used for pallet stretch wrap (pre-stretch), high performance draw down films and other mono layer and coextruded film applications where high strength is required. The grade is also suggested for blending with ethylene/butene copolymer LLDPE and LDPE for improving strength. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:LLDPE Linear low density polyethylene
用途:薄膜;流延薄膜;混合;拉伸缠绕;
加工条件:流延薄膜
性能特点: 热稳定性好; 机械强度好-撕裂; 抗氧化; 己烯共聚单体; 低密度; 韧性好; 光学性能; 抗穿孔性; Good flexibility,Optical performance,Inoxidizability,Low density,Good tear strength,Puncture Resistant,Hexene copolymers,Heat Stabilized
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.2 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
Elastic Recovery(铸造薄膜,20.0 µm) Elastic Recovery (cast film, 20.0 µ m) |
56 | % | ASTM D5459 |
Protrusion Puncture Resistance - 铸造薄膜(20.0 µm) Corrosion Function Resistance - Cast thin film (20.0 µ m) |
1.90 | J | ASTM D5748 |
Retention Force(60 sec,20.0 µm) Retention Force(60 sec,20.0 µm) 2 |
g | ||
Stress Retention(铸造薄膜,20.0 µm) Stress Retention (cast film, 20.0 µ m) |
% | ASTM D5459 | |
Ultimate Pre(stretch Level 铸造薄膜,20.0 µm) Ultimate Pre-stretch Level - Cast Film (20.0 µm) |
% | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,20 µm,铸造薄膜 45 °, 20 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
% | ASTM D1003A | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
落锤冲击 Drop hammer impact |
|||
20.0 µm,铸造薄膜 20.0 µ m, cast thin film |
J/cm | ISO 7765-2 | |
Peel Cling Peel Cling 2 |
ASTM D5458 | ||
0% pre-stretch:20.0 µm 0% pre-stretch:20.0 µm |
g/2.5 cm | ASTM D5458 | |
200% pre-stretch:20.0 µm 200% pre-stretch:20.0 µm |
g/2.5 cm | ASTM D5458 | |
撕裂强度 tear strength 2 |
|||
TD,20 µm TD,20 µm 2 |
kN/m | ISO 6383-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 Cast Film |
【新闻资讯】查看全部
帝斯曼宣布调涨PA6/66及PBT价格
2020-11-24 搜料网资讯: 继多家行业巨头调涨PA价格后,帝斯曼也于11月20日宣布提高Akulon、Novamid、TufnylPA6/66以及Arnite和Tufbet PBT的价格。 此次调价将于2020年12月1日或在合同允许的时间起生效。具体 |
帝斯曼宣布调涨PA6/66及PBT价格 搜料网资讯:继多家行业巨头调涨PA价格后,帝斯曼也于11月20日宣布提高Akulon®、Novamid®、Tufnyl®PA6/66以及Arnite®和Tufbet® PBT的价格。 此次调价将于2020年12月1日或在合同允许的时间起生效。具体涨幅如下:
帝斯曼工程材料公司表示,将继续推行和实施旨在吸收原材料上涨影响的成本节约措施。此次提价对于确保帝斯曼工程材料公司作为工程材料领先供应商的长期地位是必要的。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。