牌号简介 About |
---|
3M Dyneon聚四氟乙烯细粉TF 2029Z适用于电工胶带和各种纱线应用,如牙科、纺织、缝纫、过滤和建筑用纱线。特殊特性符合ASTM D 4895 I型1级B类高分子量聚四氟乙烯粉末,由乳液聚合制成,适用于低还原率范围,优良的化学惰性,低摩擦性能,在标准糊状物挤压加工过程中提供高拉伸比,高阻燃性,异常耐温性很好的电性能 Dyneon™ TF 2029 Z PTFE is an ideal grade for tapes with high mechanical strength, such as electrical tape for wrapped insulations or flat cables. Also ideal for yarn applications, including sewing and weaving yarn for filter and sealing materials. Product Features: High molecular weight Designed for low reduction ratios High stretch ratio Processable by standard paste extrusion methods Can be used to extrude pipe liners requiring high green strength Meets ASTM D4895-04 Type 1, Grade 1, Class B classification |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
2.15 | g/cm³ | ISO 12086 |
表观密度 Apparent density |
0.45 | g/cm³ | ISO 60 |
平均颗粒尺寸 Average particle size |
640 | µm | ISO 13320 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
34.0 | MPa | ISO 527-3 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
380 | % | ISO 527-3 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
挤出压力 Extrusion pressure |
|||
Reduction Ratio 400 Reduction Ratio 400 |
MPa | ASTM D4895 | |
Reduction Ratio Reduction Ratio |
内部方法 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我高功能碳纤维产品无望替代进口
2016-02-16 碳纤维是新材料界的宠儿,有“黑色黄金”之称,多年来我国高性能碳纤维依赖进口。如今,这一局面被黑龙江省碳纤维复合材料龙头企业、哈尔滨天顺化工科技开发有限公司打破。日前,由该公司承担的黑龙江省科技攻关重大项目“T700级碳纤维碳化中试生产线及工艺研究”,通过了黑龙江省科技厅组织的专家鉴定。 由我国复合材料学会理事长杜善义院士为主任委员的鉴定委员会认为,天顺公司以自主研制生产的碳纤维原丝为原料,经过工艺优化,所研发的具有完全自主知识产权的碳纤维生产工艺及装备技术达到国际先进水平, |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |