牌号简介 About |
---|
ACRYLITE® M30丙烯酸系聚合物系基于聚甲基丙烯酸甲酯(PMMA)之非晶形热塑性模塑料。丙烯酸酯类聚合物的典型性能有:优异的耐候性、高透光性、高机械强度、高表面硬度和抗损伤性、良好的熔体流动速率、多功能的着色性。ACRYLITE® M30聚合物的特殊性能有:中耐热性、高熔体流动速率、紫外光透射剂。G中等润滑等级应用:用于注塑光学及工艺零件。 ACRYLITE® M30 acrylic polymer is an amorphous thermoplastic molding compound based on polymethyl methacrylate (PMMA). Typical properties of ACRYLITE® acrylic polymers are: excellent weather resistance high light transmission high mechanical strength high surface hardness and mar resistance good melt flow rate versatile colorability due to crystal clarity The special properties of ACRYLITE M30 polymer are: medium heat resistance high melt flow rate UV light transmitting medium levels of lubricant Application: Used for injection molding optical and technical parts. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.19 | g/cm³ | ASTM D792 |
表观密度 Apparent density |
0.66 | g/cm³ | ASTM D1895 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,3.80kg 230℃,3.80kg |
24 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.30 to 0.60 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
平衡 balance |
< 0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火,6.35 mm 1.8 MPa, annealed, 6.35 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:0~156℃ MD:0~156℃ |
1/℃ | ASTM D696 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
透光率 Transmittance |
|||
3200 µm 3200 µm |
% | ASTM D1003 | |
雾度 Haze |
|||
3200 µm 3200 µm |
% | ASTM D1003 | |
黄度指数 Yellowness index |
|||
3.20 mm 3.20 mm |
YI | ASTM D1925 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
M 级 M-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
这些塑机企业是如何将他人的优势转化成本身利器的?
2017-09-08 一家成功的企业往往都是懂得充分利用资源的企业,他们即使是在不具备所需资源的条件下也会竭尽全力寻找与自身匹配的资源。换言之,企业必须掌握强强联手之道,懂得以他人之长弥补自身之短,将别人的优势转化为自身利器,从而实现利益最大化。企业正是因为有了合作精神,才有了长足的发展。 德国Fröbel公司与威猛巴顿菲尔 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |