牌号简介 About |
---|
Adsyl 7572 XCP是一种新的高级聚烯烃,专门设计用于共挤薄膜应用中的密封层。该等级具有极低的密封起始温度(<100°C)和优良的光学性能。不含防滑或防堵添加剂。有关监管信息,请参阅Adsyl 7572 XCP产品管理公告(PSB)。 Adsyl 7572 XCP is a new advanced polyolefin, specially designed for use as a sealing layer in co-extruded film applications. This grade features a very low seal initiation temperature (<100°C) and excellent optical properties. It does not contain slip or anti-block additives. For regulatory information please refer to Adsyl 7572 XCP Product Stewardship Bulletin (PSB). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
5.5 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
ISO 527-3/25 | ||
MD,50 µm,铸造薄膜 MD, 50 µ m, cast thin film |
260 | MPa | ISO 527-3/25 |
TD,50 µm,铸造薄膜 TD, 50 µ m, cast thin film |
250 | MPa | ISO 527-3/25 |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
MD,屈服,50 µm,吹塑薄膜 MD, yield, 50 µ m, blow molded film |
14.0 | MPa | ISO 527-3/500 |
TD,屈服,50 µm,吹塑薄膜 TD, yield, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸强度 tensile strength |
ISO 527-3/500 | ||
MD,断裂,50 µm,吹塑薄膜 MD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
TD,断裂,50 µm,吹塑薄膜 TD, fracture, 50 µ m, blow molded film |
MPa | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
MD,断裂,50 µm,铸造薄膜 MD, fracture, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
TD,断裂,50 µm,铸造薄膜 TD, fracture, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
拉伸应变 Tensile strain |
ISO 527-3/500 | ||
MD,屈服,50 µm,铸造薄膜 MD, yield, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
TD,屈服,50 µm,铸造薄膜 TD, yield, 50 µ m, cast thin film |
% | ISO 527-3/500 | |
始封温度 Initial sealing temperature |
℃ | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50.0 µm,铸造薄膜 45 °, 50.0 µ m, cast thin film |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm,铸造薄膜 50 µ m, cast thin film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
泰和新材拟开展芳纶复合资料高端装备领域应用
2016-03-10 泰和新材公告,为发挥各自优势、共享芳纶复合材料在航空市场等高端装备领域的增长,中航拓普瑞思航空技术(北京)有限公司(以下简称“中航拓普瑞思”)与公司于3月4日签署《战略合作框架协议》。公司股票3月7日复牌。 根据中航拓普瑞思提供的资料,该公司隶属中航工业集团航空装备公司,专业从事航空仿真训练系统研发及制造,是目前中航企业中唯一专门将综保体系中的技术资料、训练及训练设备和保障设备作为研制对象的公司。 公司表示,协议如能顺利实施,公司将打破国际大公司对航空市场的 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |