牌号简介 About |
---|
SABIC PP化合物7705 SABIC® PPcompound 7705是一种填充矿物的改性聚丙烯。这种材料结合了高耐刮性、高刚度、良好的冲击性和高流动性。这种材料具有很宽的加工窗口和良好的物理性能。典型应用包括美观的汽车内部零件,如仪表板、上下仪表板、门板和装饰件。SABIC® PPcompound 7705是指定的汽车级。SABIC PP化合物7705 SABIC PP化合物7705是一种矿物填充、冲击改性的聚丙烯TPO。这种材料结合了抗冲击,耐刮擦,热稳定性和汽车内部紫外线稳定性。IMDS是16161010。 SABIC® PPcompound 7705 is a mineral filled modified polypropylene. This material combines high scratch resistance, high stiffness, good impact and high flow. This material has a very broad processing window combined with good esthical performance. Typical applications include esthetical automotive interior parts such as instrument panels, lower and upper dashboard, door panels and trim. SABIC® PPcompound 7705 is a designated automotive grade. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PP PP not specified
用途:汽车领域的应用;汽车仪表板;汽车内部装备;汽车内部零件;
加工条件:注射成型 Injection Molding
性能特点: 机械强度好; 热稳定性好; 耐刮擦; 流动性高; 冲击性能好; 耐候抗UV; Good Rigidity,Weather resistance is good,High impact resistance,High liquidity,High scratch resistance,Heat Stabilized
紫外线:UV Stabilized
填料:矿物
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.05 | g/cm³ | ASTM D792 |
密度 Density |
1.04 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
22 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
60 | ISO 868 | |
拉伸模量 Tensile modulus 2 |
1910 | MPa | ASTM D638 |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/1A/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 3 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 4 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
屈服 yield 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
50 mm跨距 50 mm span 4 |
MPa | ISO 178 | |
50 mm跨距 50 mm span 5 |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ 6 |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ 7 |
ISO 179/1eA | ||
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 6 |
ISO 180/1A | ||
23℃,3.2mm 23℃,3.2mm 8 |
J/m | ASTM D256 | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
0℃ 0℃ |
kJ/m² | ISO 180-1A | |
23℃ 23℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 8 |
|||
23℃,3.2 mm 23℃,3.2 mm 8 |
ASTM D4812 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 9 |
ASTM D3763 | ||
-30℃,Energy at Peak Load -30℃,Energy at Peak Load |
J | ASTM D3763 | |
0℃,Energy at Peak Load 0℃,Energy at Peak Load |
J | ASTM D3763 | |
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 6 |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed 6 |
℃ | ISO 75-2/A | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火 0.45 MPa, unannealed 6 |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-30~100℃ TD:-30~100℃ |
1/℃ | ISO 11359-2 | |
MD:-30~100℃ MD:-30~100℃ |
1/℃ | ISO 11359-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 2.0 in/min |
4 0.079 in/min |
5 0.051 in/min |
6 方法 I (三点负荷) |
7 80*10*4mm, Cut |
8 80*10*4 mm, Cut |
9 63.5*12.7*3.2mm, Cut |
10 21.7 ft/sec |
【新闻资讯】查看全部
总体进度70.5%!呼和浩特石化PDH项目稳步推进
2022-05-31 5月27日下午,呼和浩特石化公司执行董事、党委书记刘至祥,总经理、党委副书记胡晓荣一起深入丙烷脱氢项目的施工现场,了解与掌握工程进展情况,并就进一步做好下一阶段工作提 |
总体进度70.5%!呼和浩特石化PDH项目稳步推进 5月27日下午,呼和浩特石化公司执行董事、党委书记刘至祥,总经理、党委副书记胡晓荣一起深入丙烷脱氢项目的施工现场,了解与掌握工程进展情况,并就进一步做好下一阶段工作提出了工作要求。
5万吨/年丙烷脱氢装置,目前设计和采购已完成,主要设备、材料已到货,现场施工变电所已封顶,土建、地管、主要钢结构已施工完成,主要设备安装就位,具备大面积管道安装的条件,电气、仪表也已开始施工。项目总体进度70.5%,其中设计已全部完成,采购进度85%,施工进度39%。6、7月将迎来现场施工安装的高潮,主要包括变电所内设备安装、两器内件安装、压缩机安装调试、工艺管道安装和试压、现场电气仪表安装等。计划8月主要是进行设备及电仪调试、施工收尾、三查四定问题整改等,8月30日实现中交。
据搜料网了解,5万吨/年丙烷脱氢项目是中国石油大学(华东)和华东设计院经过近十年研发,开发出的具有自主知识产权的非金属环保型流化床丙烷催化脱氢制丙烯成套技术。该技术已完成了小试、中试,中试结果在万吨级工业试验装置上进行了初步验证,核心技术已获得国家发明专利授权。5万吨/年丙烷脱氢装置一旦投产将填补国内空白,为炼厂低碳烷烃找到出路,为中国石油炼化转型提供技术支撑。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。