牌号简介 About |
---|
LNP*Faradex*WX94736是一种基于含不锈钢的PBT树脂的化合物。这种材料的附加特性包括:EMI/RFI屏蔽、导电。又名:lnp*faradex*化合物PDX-W-94736产品再订购名称:WX94736 LNP* FARADEX* WX94736 is a compound based on PBT resin containing Stainless Steel. Added features of this material include: EMI/RFI Shielding, Electrically Conductive. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PBT polybutylene terephthalate
加工条件:注射成型 Injection Molding
性能特点: 导电; 电磁屏蔽; 射频屏蔽; Conductive,EMI,RFI
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
-- -- |
1.50 | g/cm³ | ISO 1183 |
-- -- |
1.51 | g/cm³ | ASTM D792 |
收缩率 Shrinkage rate |
|||
MD:24 hrs MD:24 hrs |
0.80 到 1.0 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
1.0 到 1.2 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
1.1 | % | ISO 294-4 |
MD:24 hrs MD:24 hrs |
% | ISO 294-4 | |
吸水率 Water absorption rate |
|||
24hr,50% RH 24hr,50% RH |
% | ASTM D570 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 2 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2 | |
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 3 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ 3 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
-- -- |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Bf | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 4 |
℃ | ISO 75-2/Af | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831,ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 |
备注 |
---|
2 50 mm/min |
3 80*10*4 |
4 80*10*4 mm |
【新闻资讯】查看全部
杜邦Zytel激光透明无卤尼龙树脂获第56届R&D 100大奖
2018-12-13 近日, 杜邦 交通运输和先进材料事业部生产的无卤尼龙树脂 ZytelHTN LTFR52G30NH BL662 被评为第55届年度RD100大奖。 关于 ZytelHTN 高性能聚酰胺 ZytelHTN LTFR52G30NH BL662 是一种30%玻纤增强,可激光 |
杜邦Zytel激光透明无卤尼龙树脂获第56届R&D 100大奖 近日,杜邦交通运输和先进材料事业部生产的无卤尼龙树脂Zytel®HTN LTFR52G30NH BL662被评为第55届年度R&D100大奖。
|
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。