牌号简介 About |
---|
ATTANE™ 4606GC超低密度乙烯/己烯共聚物是一种铸膜中的表皮层,具有优异的低温热粘性能,同时具有优异的撕裂和冲击强度。在拉伸膜应用中,ATTANE™ 4606GC超低密度乙烯/己烯共聚物树脂具有优异的拉伸性能,以及良好的物理和粘附性能。ATTANE™ 4606GC超低密度乙烯/己烯共聚物树脂也可用于吹塑薄膜共挤,在吹塑薄膜共挤过程中,它与其他具有良好气泡稳定性的树脂结合,使得ATTANE™ 4606GC超低密度乙烯/己烯共聚物树脂可作为多层薄膜结构中的密封剂。应用:浇铸和吹塑薄膜中浇铸拉伸薄膜密封剂的粘层符合:欧洲委员会法规(欧盟),2011年10月,美国食品和药物管理局FCN 741,详细信息请参考法规。 ATTANE™ 4606GC Ultra Low Density Ethylene/Hexene Copolymer is a skin layer in cast film offers excellent low temperature hot tack properties combined with outstanding tear and impact strength. In stretch film applications, ATTANE™ 4606GC Ultra Low Density Ethylene/Hexene Copolymer Resin exhibits excellent stretchability as well as good physical and cling properties. ATTANE™ 4606GC Ultra Low Density Ethylene/Hexene Copolymer Resin can also be utilised in blown film coextrusion where it is combined with other resins having excellent bubble stability allowing ATTANE™ 4606GC Ultra Low Density Ethylene/Hexene Copolymer Resin to be used as a sealant in multilayer film structures. Applications: Cling layer in cast stretch film Sealants in cast and blown films Complies with: Europe Commission Regulation (EU), No 10/2011 U.S. FDA FCN 741 Consult the regulations for complete details. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.911 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
3.3 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
23 | µm | |
膜刺穿强度 Membrane puncture strength |
|||
23 µm 23 µm |
2.80 | J | ASTM D5748 |
膜刺穿力 Membrane puncture force |
|||
23 µm 23 µm |
35.0 | N | ASTM D5748 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,23 µm MD, yield, 23 µ m |
MPa | ISO 527-3 | |
TD,屈服,23 µm TD, yield, 23 µ m |
MPa | ISO 527-3 | |
MD,断裂,23 µm MD, fracture, 23 µ m |
MPa | ISO 527-3 | |
TD,断裂,23 µm TD, fracture, 23 µ m |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,23 µm MD, fracture, 23 µ m |
% | ISO 527-3 | |
TD,断裂,23 µm TD, fracture, 23 µ m |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
23 µm 23 µm |
g | ISO 7765-1/A | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:23 µm MD:23 µm |
g | ASTM D1922 | |
TD:23 µm TD:23 µm |
g | ASTM D1922 | |
未拉伸粘结 Unstretched bonding |
g | ASTM D4649 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,23 µm 45°,23 µm |
ASTM D2457 | ||
雾度 Haze |
|||
23 µm 23 µm |
% | ASTM D1003 |
备注 | |||
---|---|---|---|
暂无数据 |
【新闻资讯】查看全部
美国修正对华聚对苯二甲酸乙二醇酯树脂反补贴案
2016-05-10 2016年5月6日,美国商务部发布公告称,应DAK Americas、M&G Chemicals和 Nan Ya Plastics Corporation于2016年3月14日提交的申请,修改对华聚对苯二甲酸乙二醇酯树脂(Polyethylene Terephthalate Resin)反补贴案终裁结果和征税令:江阴兴宇新材料有限公司(Jiangyin Xingyu New Material Co., Ltd.)等15家公司和中国普遍补贴幅度分别上调至7.53%和 27.55%。美 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |