牌号简介 About |
---|
HANWHA LLDPE 3325W采用滚圆工艺制造,适用于各种薄膜应用,如保护膜和拉伸包装膜。LLDPE 3325W具有良好的机械性能和加工性能的平衡性。 HANWHA LLDPE 3325W is manufactured by Spherilene process and designed for variety of film application such as protective film and stretch wrap film. LLDPE 3325W has well balanced property of mechanical property and processability. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.911 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.0 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
20 | µm | |
拉伸强度 tensile strength |
ASTM D882 | ||
断裂 fracture |
18.6 | MPa | ASTM D638 |
MD,断裂,20 µm MD, fracture, 20 µ m |
39.2 | MPa | ASTM D882 |
TD,断裂,20 µm TD, fracture, 20 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain |
ASTM D882 | ||
断裂 fracture |
% | ASTM D638 | |
MD,断裂,20 µm MD, fracture, 20 µ m |
% | ASTM D882 | |
TD,断裂,20 µm TD, fracture, 20 µ m |
% | ASTM D882 | |
落锤冲击 Drop hammer impact |
|||
20 µm 20 µm |
g | ASTM D1709 | |
撕裂强度 tear strength |
ASTM D1004 | ||
MD,20 µm MD,20 µm |
kN/m | ASTM D1004 | |
TD,20 µm TD,20 µm |
kN/m | ASTM D1004 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
熔融峰值温度 Melting peak temperature |
℃ | 内部方法 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
雾度 Haze |
|||
20 µm 20 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
5月21日国内PE装置动态汇总
2021-05-21 搜料网资讯: 地区 厂家名称 产能 品种 5月21日 用途 东北地区 大庆石化 7.8 LLDPE 8320 线性 7 HDPE装置A线 5000S 低压拉丝 7 HDPE装置B线 5000S 低压拉丝 10 HDPE装置C线 QL505P 其他 6.5 老LDPE 18D0 高压 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |