牌号简介 About |
---|
Kynar-flex 2750-01是一种基于VF2的半结晶共聚物。它是为需要高灵活性和提高抗冲击性的应用而设计的。Kynar flex 2750-01可用于挤出和注塑工艺。附加特性:优异的热稳定性、优异的耐磨性、优异的纯度和抗紫外线降解的化学性能、自熄材料极低的烟雾发射特性、可着色的Kynar flex 2751-00是本产品的粉末版。 Kynar Flex® resins are fluorinated thermoplastic copolymers. Outstanding characteristics: chemical resistance, imperviousness to UV, barrier properties and high purity. Main applications: flexible tubing, corrosion protection in the chemical industry, off-shore, wire and cable. Kynar Flex® 2751-00 resin is a powder grade where maximum flexibility or impact strength is required. |
技术参数 Technical Data | |||
---|---|---|---|
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature |
130 到 138 | ℃ | ASTM D3418 |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity 2 |
|||
20 ℃ 20 ℃ 2 |
2.0E+14 | ohms·cm | ASTM D257 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D,23℃ Shore D, 23 ℃ |
55 到 62 | ASTM D2240 | |
拉伸强度 tensile strength |
ASTM D638 | ||
屈服,23℃ Yield, 23 ℃ |
13.8 到 21.4 | MPa | ASTM D638 |
断裂,23℃ Fracture, 23 ℃ |
20.0 到 27.6 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
压缩强度 compressive strength |
|||
23℃ 23℃ |
MPa | ASTM D695 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ASTM D792 | |
熔体表观粘度 Apparent viscosity of melt |
|||
232℃,100 sec^-1 232℃,100 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 65% R.H. |
【新闻资讯】查看全部
科思创:加速布局医疗健康、交通出行、电子电气等更多领域
2021-06-25 搜料网资讯: 1953年,全球最大的聚碳酸酯生产商科思创的前身拜耳公司发明了聚碳酸酯。它可应用于电子电器、汽车和医疗等多个行业,是五大工程塑料之一。2020年,聚碳酸酯贡献了 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |