牌号简介 About |
---|
KetaSpire KT- 880 FW30是高流动性 、30 %碳纤增强聚醚醚酮( PEEK)。 在温度接近300℃时,碳纤增强 KetaSpire PEEK 的机械性能达到行业最高水平,并且,具有KetaSpire 产品系列最低的线性热膨胀系数。KetaSpire PEEK按照最高的行业标准加工,以兼具各种出色的性能为特征,包括优异的耐磨损性、一流的抗疲劳性、易于熔融加工、高纯度、优异的耐有机物、酸和碱等化学物质的性能。 这些特性使得它非常适合医疗保健、交通运输、电子、化学处理和其它工业用途。 KetaSpire® KT-880 FW30 is a polyetheretherketone (PEEK) compound with higher flow than KetaSpire® KT-820 SL30, making it more suitable for injection molding applications. It is designed to deliver a balance of excellent mechanical properties, wear resistance and low coefficient of friction in both dry and externally lubricated applications. The resin is formulated with anti-friction/anti-wear additive system comprised of carbon fiber and polytetrafluoroethylene (PTFE). KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases. These properties make it well-suited for applications in transportation, electronics, chemical processing, and industrial uses including oil and gas exploration and production. The resin is black in color in its natural state. |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-- -- |
68 | J/m | ASTM D256 |
-- -- |
7.0 | kJ/m² | ISO 180 |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
530 | J/m | ASTM D4812 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
玻璃化转变温度 Glass transition temperature |
147 | ℃ | ISO 11357-2 |
熔融温度 Melting temperature |
343 | ℃ | ISO 11357-3 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2 | |
-- -- |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- |
MPa | ASTM D790 | |
-- -- |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ASTM D695 | |
剪切强度 shear strength |
MPa | ASTM D732 | |
摩擦系数 friction coefficient |
ASTM D3702 | ||
磨损因数 Wear factor |
|||
0.22 MPa,4.1 m/sec 0.22 MPa,4.1 m/sec |
10^-8 mm³/N·m | ASTM D3702 | |
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体质量流动速率 Melt Flow Rate |
|||
400℃,5.0kg 400℃,5.0kg |
g/10min | ASTM D1238 | |
PV Limit PV Limit |
psi·fpm | ||
熔体表观粘度 Apparent viscosity of melt |
|||
400℃,1000 sec^-1 400℃,1000 sec^-1 |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 GMW 16771-Sequence B |
3 Dry |
【新闻资讯】查看全部
石墨烯未来将在塑料五大领域大显身手
2017-12-04 ●石墨烯具有优异的导电性能,且长径比较大。 ●石墨烯添加到塑料中后,能使塑料的热导率提高10倍以上。 ●石墨烯的机械强度是钢的100倍,可极大提高塑料的机械性能。 ●石墨烯表面改性后可附加不同的基团,做出智能材料。 CPRJ&SPE新材料高峰会的脚步越来越近,筹备工作已进入紧锣密鼓的准备阶段。这是一场汇聚国内外添加剂与改性塑料行业精英的年度盛会,许多行业大咖已确认参加论坛。 国家“千人计划”海外特聘专家 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |