牌号简介 About |
---|
PA 66采用10%玻璃纤维和20%玻璃珠进行化学增强。改善收缩的各向异性。玻璃纤维和玻璃微珠的理想组合可以改变各向异性与力学性能的关系。表面亮度高,滚动阻力小。精确零件的制造/主要是平面/空气管道中的节流阀。由于添加了玻璃纤维,拉伸强度和拉伸模量增加。以完整的RAL色标交付。 PA 66 chemically reinforced with 10 % glass fibre and with the content of 20% glass beads. Improved anisotropy of shrinkage. The relation of the anisotropy to the mechanical properties can be changed by the ideal combination of the glass fibre and the glass beads. High surface brightness, low rolling resistance force. Manufacturing of exact parts /mainly in flat form/, throttle valves in air piping. Increased strength and tension modulus in tension due to the addition of glass fibre. Delivered in the full RAL colour scale. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.36 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
275℃,0.325kg 275℃,0.325kg |
1.0 | g/10min | ISO 1133 |
收缩率 Shrinkage rate |
STM 64 0808 | ||
TD TD |
1.6 | % | STM 64 0808 |
MD MD |
1.0 | % | STM 64 0808 |
含水量 water content |
0.15 | % | ISO 960 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
MPa | ISO 527-2 | |
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
拉伸应变 Tensile strain |
|||
屈服 yield |
% | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179 | ||
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179 | ||
-20℃ -20℃ |
kJ/m² | ISO 179 | |
23℃ 23℃ |
kJ/m² | ISO 179 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/B | |
熔融温度 Melting temperature |
|||
DSC DSC |
℃ | ISO 3146 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
℃ | IEC 60695-2-13 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
杜邦推出Zytel®和Hytrel®系列以满足电子产业需…
2017-05-18 杜邦高性能材料事业部面向性能驱动型笔记本电脑市场推出了新一代结构式外壳材料。杜邦Zytel® HTN高温尼龙产品和高性能热塑性聚酯弹性体Hytrel®实现了市场急需材料解决方案以实现设备 “更薄、更轻、更坚固”的行业需求。 杜邦新一代Zytel® HTN高温尼龙产品具有超过19 GPa的弯曲模量,同时具有高韧性、高流动性,且适合快速成型、易于喷涂,适用于轻便型笔记本电脑结构外壳部件,例如:笔记本的A面(LCD外壳),D面(底壳)以及C框架的理想选材。这种材料能够以合理的价格 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |