牌号简介 About |
---|
NANCAR® 1052M43是一种中高丙烯腈-丁二烯共聚物,具有良好的耐油性。这是南卡1052的低穆尼版本。低门尼在高填充或增强化合物中提供最佳的加工性能。NANCAR® 1052M43,类似于南卡1052,是一种优秀的多用途丁腈弹性体。特别推荐用于鞋、辊、转移成型或挤压以及摩擦或涂层织物。 NANCAR® 1052M43 is a medium high acrylonitrile butadiene copolymer with good oil resistance. It is a low Mooney version of NANCAR 1052. The low Mooney provides optimum processing property in highly filled or reinforced compounds. NANCAR® 1052M43 , similar to NANCAR 1052, is an excellent multi-purpose nitrile elastomer. It is particularly recommended for shoes, rolls, transfer molding or extrusion and for frictioning or coating fabrics. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.980 | g/cm³ | |
门尼粘度 Mooney viscosity |
|||
ML 1+4,100℃ ML 1+4,100℃ |
43 | MU | ASTM D1646 |
丙烯腈含量(Bound) Acrylonitrile content (Bound) |
33.0 | % | 内部方法 |
Stabilizer Stabilizer |
Non-staining | ||
可溶性 solubility |
|||
in MEK in MEK |
100 | % | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 A Shaw's A 2 |
ASTM D2240 | ||
邵氏 A Shaw's A 3 |
ASTM D2240 | ||
邵氏 A Shaw's A 4 |
ASTM D2240 | ||
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
300% 应变 300% strain 5 |
MPa | ASTM D412 | |
300% 应变 300% strain 6 |
MPa | ASTM D412 | |
300% 应变 300% strain 7 |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ASTM D412 | ||
屈服 yield 2 |
MPa | ASTM D412 | |
屈服 yield 3 |
MPa | ASTM D412 | |
屈服 yield 4 |
MPa | ASTM D412 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture 5 |
% | ASTM D412 | |
断裂 fracture 6 |
% | ASTM D412 | |
断裂 fracture 7 |
% | ASTM D412 | |
撕裂强度 tear strength 8 , 3 |
kN/m | ASTM D624 | |
压缩形变 Compression deformation 4 |
|||
100℃,70 hr 100℃,70 hr 4 |
% | ASTM D395 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air 3 |
|||
100℃,70 hr 100℃,70 hr 3 |
% | ASTM D865 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air 3 |
|||
100℃,70 hr 100℃,70 hr 3 |
% | ASTM D865 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air 3 |
|||
邵氏 A,100℃,70 hr Shore A, 100 ℃, 70 hr 3 |
ASTM D865 | ||
拉伸强度的变化率 The rate of change in tensile strength 3 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
极限伸长率的变化率 Change rate of ultimate elongation 3 |
ASTM D471 | ||
100℃,70 hr,在ASTM #1油中 100 ℃, 70 hr, in ASTM # 1 oil |
% | ASTM D471 | |
100℃,70 hr,在ASTM #3油中 100 ℃, 70 hr, in ASTM # 3 oil |
% | ASTM D471 | |
邵氏硬度的变化率 The rate of change in Shore hardness 3 |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #1油中 Support A, 100 ℃, 70 hr, in ASTM # 1 oil |
ASTM D471 | ||
支撐 A,100℃,70 hr,在ASTM #3油中 Support A, 100 ℃, 70 hr, in ASTM # 3 oil |
ASTM D471 | ||
体积变化 Volume change 3 |
ASTM D471 | ||
100℃,70 hr,ASTM 标准油(1号) 100 ℃, 70 hr, ASTM standard oil (No.1) |
% | ASTM D471 | |
100℃,70 hr,ASTM 标准油(3号) 100 ℃, 70 hr, ASTM standard oil (No.3) |
% | ASTM D471 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热损耗 Heat loss |
% | ASTM D5688 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 硫化 20.0 min 在 302°F |
3 硫化 40.0 min 在 302°F |
4 硫化 60.0 min 在 302°F |
5 Cured for 60.0 min at 150°C |
6 Cured for 40.0 min at 150°C |
7 Cured for 20.0 min at 150°C |
8 C 模具 |
【新闻资讯】查看全部
淄博绿色化工产业研究院揭牌
2021-07-08 搜料网资讯: 图为揭牌仪式现场。(高艳 摄) 7月8日,中国淄博绿色化工新材料产业发展大会暨淄博绿色化工产业研究院揭牌及临淄区化工产业高质量发展战略咨询委员会成立大会在淄博 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |