牌号简介 About |
---|
EBALTA 120/GL是一种低粘性双组分环氧树脂,具有高强度和快速固化的特点。由于这种树脂/硬化剂混合物具有良好的浸水和润湿特性,因此最适用于玻璃纤维或碳纤维织物的固体零件。AH 120/GL适用于大面积和厚层压板的层压树脂。由于其几乎无气味和皮肤友好的GL硬化剂,它是最适合作为层压树脂。当混合比为100:40时,玻璃化转变温度(Tg)会升高约15°C,层压板会稍微变硬,抗冲击性也会更好。层压板厚度不应超过6-7 mm。层压树脂在织物、车辆、飞机结构中的应用无填充低粘度、高强度、低放热特性 ebalta 120/GL is a very low-viscous two-component epoxy resin with high strength values and fast curing. Due to its good soaking and wetting characteristics, this resin/hardener mixture is most suitable for solid parts with fabrics made of glass or carbon fibres. AH 120/GL is suitable as laminating resin for both large area- and thick laminates. Due to its almost odourless and skin-friendly GL hardener it is most suitable as laminating resin. With a mixing ratio of 100:40 you reach an about 15°C higher TG, slightly stiffer laminates as well as better impact resistance. The laminate thickness should not exceed 6-7 mm. Applications Laminating resin for fabrics Vehicle construction Aircraft construction Properties unfilled low viscosity high strength low exothermic character |
技术参数 Technical Data | |||
---|---|---|---|
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
43 到 53 | kJ/m² | ISO 179 |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
20℃ 20℃ |
1.09 到 1.13 | g/cm³ | |
粘度 viscosity |
|||
25℃ 25℃ |
0.83 到 1.0 | Pa·s | |
固化时间 Curing time |
|||
20℃ 20℃ |
12 到 16 | hr | |
储存稳定性 storage stability 2 |
|||
20 ℃ 20 ℃ 2 |
40 到 45 | min | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 7619 | ||
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
压缩强度 compressive strength |
MPa | ISO 604 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
热固组件 Thermosetting components |
|||
树脂 resin |
|||
硬化法 Hardening method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 200 g |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |