牌号简介 About |
---|
符合ISO 1043-1的化学缩写:POM成型化合物ISO 9988-POM-K,M-GNR,02-003,GF26 POM共聚物注射成型型,用Ca 26%玻璃纤维增强;高耐热性和氧化降解性;减少热膨胀和收缩。所有颜色和厚度超过1.57 mm的UL注册为UL 94 HB,温度指数为UL 746 B,电气105°C,机械95°C(拉伸冲击)和100°C(拉伸)。燃烧速率ISO 3795和FMVSS 302<100 mm/min,厚度大于1 mm。适用范围:适用于高强度、高刚度、高硬度的成型件。fmvss=联邦机动车安全标准(美国)ul=保险商实验室(美国) Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 02-003, GF26 POM copolymer Injection molding type, reinforced with ca 26 % glass fibers; high resistance to thermal and oxidative degradation; reduced thermal expansion and shrinkage. UL-registration for all colours and a thickness more than 1.57 mm as UL 94 HB, temperature index UL 746 B electrical 105 °C, mechanical 95 °C (tensile impact) and 100 °C (tensile). Burning rate ISO 3795 and FMVSS 302 < 100 mm/min and a thickness more than 1 mm thickness. Ranges of applications: For molded parts with very high strength and rigidity as well as higher hardness. FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA) |
技术参数 Technical Data | |||
---|---|---|---|
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
9200 | MPa | ISO 527-2/1A/1 |
拉伸强度 tensile strength |
|||
断裂 fracture |
135 | MPa | ISO 527-2/1A/5 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
2.5 | % | ISO 527-2/1A/5 |
Tensile Creep Modulus(1 hr) Tensile Creep Modulus(1 hr) |
7700 | MPa | ISO 899-1 |
拉伸蠕变模量 Tensile creep modulus |
|||
1000 hr 1000 hr |
5400 | MPa | ISO 899-1 |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
熔融温度 Melting temperature 2 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD TD |
1/℃ | ISO 11359-2 | |
MD MD |
1/℃ | ISO 11359-2 | |
Effective Thermal Diffusivity Effective Thermal Diffusivity |
cSt | Internal Method | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
100 Hz 100 Hz |
IEC 60250 | ||
1 MHz 1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
g/cm³ | ISO 1183 | |
熔体体积流动速率 Melt Volume Rate |
|||
190℃,2.16 kg 190℃,2.16 kg |
cm³/10min | ISO 1133 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
Density of Melt Density of Melt |
g/cm³ | Internal Method | |
Specific Heat Capacity of Melt Specific Heat Capacity of Melt |
J/kg/℃ | Internal Method | |
Thermal Conductivity of Melt Thermal Conductivity of Melt |
W/m/K | Internal Method |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 10°C/min |
【新闻资讯】查看全部
挺进上游,国恩股份布局20万吨聚丙烯!
2022-01-05 搜料网资讯: 金发科技收购海越新材料,同时在宁波规划建设120万吨/年聚丙烯热塑性弹性体及改性新材料一体化项目。塑料改性企业向上延伸产业链,不止1家企业,国恩股份也来啦! |
挺进上游,国恩股份布局20万吨聚丙烯! 搜料网资讯:金发科技收购海越新材料,同时在宁波规划建设“120万吨/年聚丙烯热塑性弹性体及改性新材料一体化项目”。塑料改性企业向上延伸产业链,不止1家企业,国恩股份也来啦! 国恩化学控股江苏国恒后,以司法拍卖的方式取得原“江苏旭升石化有限公司”位于“扬州化学工业园区油港路18号”工业房地产,承接布局年产20万吨聚丙烯(PP)树脂生产线。 通过聚丙烯(PP)树脂材料的生产,将有效实现熔喷无纺布材料、可降解材料、预涂布、BOPP电容膜等材料的一体化生产,并在汽车、家电、风电等领域连续纤维聚丙烯改性材料,实现属地生产一体化。其将切实降低产品成本,增强市场竞争力。 此次投资是基于公司2021年10月,通过全资子公司国恩化学对江苏国恒进行增资扩股的基础上完成的另一战略布局。 通过向改性材料上游聚苯乙烯(GPPS、PS)和聚丙烯(PP)树脂的纵向延伸,未来公司将通过聚苯乙烯材料,完成家电、小家电、电动工具、汽车、建筑装修装饰材料等改性材料的一体化生产布局,同时,实现在光显材料、光扩散板、膜、片材料及BOPS包材等领域的降本一体化生产。 国恩股份发布公告,近期,公司根据现场尽调和会计师事务所审计结果,收购了锦佑投资所持有的浙江一塑99%的股权计2.97亿元出资额。 2022年1月3日,公司与青岛一塑、迪一投资签署了《增资协议书》,浙江一塑注册资本由3亿元增至6亿元。其中,公司向浙江一塑增资1.23亿元,青岛一塑向浙江一塑增资1.2亿元,迪一投资向浙江一塑增资5700万元。 浙江一塑是一家年产百万吨级聚苯乙烯(PS)的化工企业,国恩股份本次增资完成后,将持有浙江一塑高达70%的股权。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
- 奥迪刹车灯框
- 2019-07-31 0
- Hostaform POM共聚物非常坚硬和僵硬,是奥迪A4中的第三个制动灯就是目前使用的Xap级hostaform车辆。由于其暴露在后窗后面,因此软管式XAP部件必须具有良好的紫外线稳定性。另外一个问题是温度的
- 阅读全文
奥迪刹车灯框
- 汽车方向盘无线电开关
- 2019-03-29 0
- Hostaform® C 9021 GV1/30是POM共聚物注射成型,材料良好的电气性质
- 阅读全文
汽车方向盘无线电开关
2-温度指数为UL 746 B,电气105°C,机械95°C(拉伸冲击)和100°C(拉伸)
3-适用于高强度、高刚度、高硬度的成型件
4-广泛的使用温度范围(-40℃~120℃)
抱歉!暂无数据。