牌号简介 About |
---|
Eltex® PF6612AA是一种产于欧洲的茂金属LLDPE级。优点和特点Eltex® PF6612AA是一种含有己烯-1作为共聚单体的聚乙烯共聚物,由茂金属催化剂制备。它具有以下特性:高冲击强度和刚性优良的光学特性非常好的气泡稳定性和可挤压性低温密封特性应用Eltex® PF6612AA已被开发用于整理收缩膜、食品包装和其他薄膜应用,在这些应用中,膜结构之间的良好平衡。要求有足够的长度和刚度以及良好的光学性能。此外,Eltex® PF6612AA提供了容易挤压。如果需要电晕处理,水平通常应在38-48mn/m范围内。 Eltex® PF6612AA is a metallocene LLDPE grade produced in Europe. Benefits & Features Eltex® PF6612AA is a polyethylene copolymer containing hexene-1 as the comonomer produced with a metallocene catalyst. It offers the following properties: High impact strength and rigidity Excellent optical properties Very good bubble stability and extrudability Low temperature sealing characteristics Applications Eltex® PF6612AA has been developed for use in collation shrinkwrap, food packaging and other thin film applications where an excellent balance between film strength and rigidity is required together with good optical properties. In addition, Eltex® PF6612AA offers easy extrudability. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.926 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.3 | g/10min | ISO 1133 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
薄膜厚度 film thickness |
|||
测试 test |
25 | µm | |
拉伸模量 Tensile modulus |
ISO 527-3 | ||
1% 正割,MD,25 µm,吹塑薄膜 1% secant, MD, 25 µ m, blow molded film |
230 | MPa | ISO 527-3 |
1% 正割,TD,25 µm,吹塑薄膜 1% secant, TD, 25 µ m, blow molded film |
270 | MPa | ISO 527-3 |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,屈服,25 µm,吹塑薄膜 MD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,屈服,25 µm,吹塑薄膜 TD, yield, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸强度 tensile strength |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
MPa | ISO 527-3 | |
拉伸应变 Tensile strain |
ISO 527-3 | ||
MD,断裂,25 µm,吹塑薄膜 MD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
TD,断裂,25 µm,吹塑薄膜 TD, fracture, 25 µ m, blow molded film |
% | ISO 527-3 | |
落锤冲击 Drop hammer impact |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
g | ASTM D1709-A | |
撕裂强度 tear strength |
|||
TD,25 µm,吹塑薄膜 TD, 25 µ m, blow molded film |
g | ASTM D1922 | |
MD,25 µm,吹塑薄膜 MD, 25 µ m, blow molded film |
g | ASTM D1922 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔融峰值温度 Melting peak temperature 2 |
℃ | ASTM D3418 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,25 µm,吹塑薄膜 45 °, 25 µ m, blow molded film |
ASTM D2457 | ||
雾度 Haze |
|||
25 µm,吹塑薄膜 25 µ m, blow molded film |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2nd heating |
【新闻资讯】查看全部
2015年全国日用塑料产量前十省市出炉 广东居首
2016-03-02 2015年1-12月全国日用塑料制品产量为592.66万吨。塑料制品产量前十的省市分别是广东、浙江、湖北、四川、江苏、河北、山东、福建、河南和天津。各省市产量依次是132.13万吨、108.83万吨、58.20万吨、49.37万吨、49.14万吨、39.71万吨、23.32万吨、22.16万吨、21.07万吨和17万吨。前三省份日用塑料制品的产量占据全国产量的50.4%。 其中,广东日用塑料制品产量为132.13万吨,占全国日用塑料制品产量的22.3%,成为全国日用塑料制品 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |