法拉第NX07344是一种以PC+ABS共混树脂为基础的复合材料,含有无溴无氯阻燃体系、不锈钢和玻璃纤维。这种材料的附加特性包括:EMI/RFI屏蔽和ESD。 Faradex NX07344 is a compound based on PC+ABS blend resin containing non-brominated and non-chlorinated flame retardant system, Stainless Steel and glass fiber. Added features of this material include: EMI/RFI Shielding and ESD. |
产品描述 Product Description
厂家:沙特沙伯基础 SABIC
类别:PC+ABS PC+ABS
加工条件:注射成型 Injection Molding
性能特点: 静电放电保护; 无卤; 防火阻燃等级V-0; 阻燃; 电磁屏蔽; 射频屏蔽; Halogen free,Electrostatic discharge protection,Flame Characteristics,EMI,RFI,V-0
填料:玻璃纤维/不锈钢纤维
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.46 | g/cm³ | ASTM D792, ISO 1183 |
收缩率 Shrinkage rate |
内部方法 | ||
MD MD |
0.38 | % | |
TD TD |
0.46 | % | |
吸水率 Water absorption rate |
|||
24hr,50% RH 24hr,50% RH |
0.080 | % | ASTM D570 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
0.040 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
-- -- 1 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂 fracture 2 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
-- -- 5 |
MPa | ISO 178 | |
屈服,50 mm跨度 Yield, 50 mm span 6 |
MPa | ASTM D790 | |
断裂,50 mm跨度 Fracture, 50 mm span 7 |
MPa | ASTM D790 | |
断裂弯曲应变 Fracture bending strain 8 |
% | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 9 |
|||
23℃ 23℃ 9 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
-30℃ -30℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
-30℃ -30℃ 10 |
kJ/m² | ISO 180-1A | |
23℃ 23℃ 11 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
-30℃ -30℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D4812 | |
-30℃ -30℃ 12 |
kJ/m² | ISO 180/1U | |
23℃ 23℃ 13 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Total Energy 23℃,Total Energy |
J | ASTM D3763 | |
-- -- |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 14 |
℃ | ISO 75-2/Af | |
维卡软化温度 Vicat Softening Temp |
|||
B120 B120 |
℃ | ASTM D1525, ISO 306/B120 12 15 | |
-- -- |
℃ | ASTM D1525 16 | |
A50 A50 |
℃ | ISO 306/A50 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:23~60℃ MD:23~60℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
TD:23~60℃ TD:23~60℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | ASTM D257 | |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
静电衰减 Electrostatic attenuation 17 |
msec | FTMS 101B | |
屏蔽效力 Shielding effectiveness |
内部方法 | ||
1.50 mm 1.50 mm |
dB | ||
3.00 mm 3.00 mm |
dB | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50 mm 1.50 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 0.079 in/min |
6 Yield |
7 2 mm/min |
8 80*10*4 sp=62mm |
9 80*10*4 |
10 80*10*4 mm |
11 标准 B (120°C/h), 载荷2 (50N) |
12 速率 A (50°C/h), 载荷2 (50N) |
13 5000V to <50V |
【新闻资讯】查看全部
科乃而:R-PRO保送零碎欧洲首秀完美收官!
2016-11-11 继CHINAPLAS 2016、TaipeiPLAS 2016之后,科乃而(Conair)的R-PRO输送系统(酯粒保护输送系统)首次在K 2016上展示,欧洲首秀完美收官! “从K 2016开展第一天开始,这台设备吸引了不少国家地区的客户前来咨询,甚至连竞争对手也前来观看交流。”科乃而亚太区总经理陈建昌先生说。“目前R-PRO输送系统主要应用于PET瓶的生产,但逐渐也有医疗管材的生产商开始采纳这一设备。” 陈建昌表示,包装仍然是科乃而的重点市场。“但是我们 |
科乃而:R-PRO保送零碎欧洲首秀完美收官! 继CHINAPLAS 2016、TaipeiPLAS 2016以后,科乃而(Conair)的R-PRO输送系统软件(酯粒维护输送系统软件)初次在K 2016上展现,欧州首次亮相圆满结束! “从K 2016进行第一天逐渐,这台机器设备吸引住了许多我国地域的顾客前去资询,乃至连竞争者也前去收看沟通交流。”科乃而亚太地区经理陈建昌老先生说。“现阶段R-PRO输送系统软件关键运用于PET瓶的生产制造,但慢慢也是有医疗管件的制造商逐渐听取意见这一机器设备。” 陈建昌表明,包裝依然是科乃而的关键销售市场。“可是大家也会逐渐渗入医疗销售市场中,此次K 2016 大家也展现了相关医疗管件生产制造的輔助机器设备,这可能是K 2016 当场唯一一台与医疗管件生产制造有关的輔助机器设备了!” 据陈建昌强调,科乃而的R-PRO输送系统软件可不在限定货运量的状况下,以低速档及更少的酯粒磨坏开展输送。传统式的塑料粒子选用负压力输送,塑料粒子在管路内必须很多的气体开展输送,基本上做到每分一英哩的速率;而髙速摩擦使塑料粒子非常容易造成烟尘、高溫、金属拉丝或头发(Angle hair)状况,非常容易使管路阻塞。 来源于:CPRJ 中国塑料硫化橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。