牌号简介 About |
---|
由IEPL利用加拿大杜邦的“SCLAIRTECH”溶液聚合工艺生产的HBG00356高密度聚乙烯树脂(现为Nova Chemicals)提供具有广泛分子量分布的中等分子量材料。作为一种共聚物,它具有很高的抗冲击性和很好的环境应力开裂性和很好的刚度,因此特别适用于生产瓶子、容器和技术性空心制品。它可以很容易地在普通的聚乙烯吹塑机上加工,使用的熔融温度在170到200°C之间。 HBG00356 High Density Polyethylene Resin manufactured by IEPL using "SCLAIRTECH" solution polymerisation process of DU Pont, Canada (Now Nova Chemicals) offers medium molecular weight material with broad molecular weight distribution. As a copolymer it combines very high impact and excellent environmental stress crack resistance with good stiffness and is therefore especially suitable for the production bottles, containers and technical hollow articles. It can be easily processed on normal polyethylene blow moulding machines, using melt temperatures between 170 and 200°C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.956 | g/cm³ | ASTM D1505 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
0.30 | g/10min | ASTM D1238 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
125 | ℃ | ASTM D1525 1 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
67 | ASTM D1706 | |
拉伸强度 tensile strength |
|||
屈服 yield |
28.1 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D747 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
一句骗过了一切塑料老板的假话
2017-11-06 在11月4日晚的美因茨客场VS.门兴德甲赛场上,上演了非常精彩的一幕,让人忍俊不禁。 比赛进行到上半场30分,美因茨门将泽特纳接到本方回传球,在自家禁区内上演神级操作,一个假 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |