牌号简介 About |
---|
OREVAC 18334是一种顺丁烯二酸酐改性线性低密度聚乙烯,以颗粒形式提供。它可以在大多数设计用于加工传统聚烯烃的挤压设备上进行加工。应用OREVAC 18334设计用于在共挤过程中开发聚乙烯或乙烯共聚物与极性树脂(如聚酰胺和EVOH)之间的可靠粘合强度。OREVAC 18334建议用于吹塑或管共挤。OREVAC 18334可作为三层管道涂层的粘合剂。 OREVAC® 18334 is a maleic anhydride modified linear low-density polyethylene available in pellet form. It can be processed on most extrusion equipment designed to process conventional polyolefins. Applications OREVAC® 18334 has been designed to develop a reliable bonding strength between polyethylene or ethylene copolymers and polar resins such as polyamides and EVOH within a coextrusion process. OREVAC® 18334 is recommended for blow moulding or tube coextrusion. OREVAC® 18334 can be used as the adhesive for three layers pipe coating. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.920 | g/cm³ | ASTM D1505 |
密度 Density |
0.920 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ISO 1133 |
190℃,2.16kg 190℃,2.16kg |
1.0 | g/10min | ASTM D1238 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,模压成型 Fracture, molded |
28.0 | MPa | ASTM D638 |
断裂,模压成型 Fracture, molded |
MPa | ISO 527-2 | |
屈服,模压成型 Yield, molding |
MPa | ISO 527-2 | |
屈服,模压成型 Yield, molding |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂,模压成型 Fracture, molded |
% | ASTM D638 | |
断裂,模压成型 Fracture, molded |
% | ISO 527-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
【干货】气辅制品和模具设计基本原则
2020-11-18 搜料网资讯: (1)设计时先考虑哪些壁厚处需要掏空,哪些表面的缩痕需要消除,再考虑如何连接这些部位成为气道。 (2)大的结构件:全面打薄,局部加厚为气道。 (3)气道应依 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |