牌号简介 About |
---|
LL4800N是一种线性低密度聚乙烯,辛烯-1共聚物,溶液法生产。开发用于铸膜挤出。用该产品获得的薄膜显示出良好的加工性能,并具有良好的机械和光学性能。它含有加工助剂和抗氧化剂添加剂。 LL4800N is a Linear Low Density Polyethylene developed for cast film extrusion. Films obtained with this product show good processing performance balanced with excellent mechanical and optical properties. It contains processing aid and antioxidant additives. Applications: Stretch films; liners; LPED and HDPE blends and packages for general use. Additive: Processing Aid Process: LL4800N must be processed in extruder of plain matrix, adjusted to this polymer. The optimum processing conditions will vary accord to the type of equipment used, but the best results are obtained with a extrusion temperature between of 220 to 270°C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.917 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,2.16kg 190℃,2.16kg |
2.1 | g/10min | ASTM D1238 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
50.0 | MPa | ASTM D882 |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
40.0 | MPa | ASTM D882 |
拉伸应变 Tensile strain |
ASTM D882 | ||
MD,断裂,40 µm,吹塑薄膜 MD, fracture, 40 µ m, blow molded film |
1200 | % | ASTM D882 |
TD,断裂,40 µm,吹塑薄膜 TD, fracture, 40 µ m, blow molded film |
% | ASTM D882 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
1% 正割,MD,40 µm,吹塑薄膜 1% secant, MD, 40 µ m, blow molded film |
MPa | ASTM D790 | |
1% 正割,TD,40 µm,吹塑薄膜 1% secant, TD, 40 µ m, blow molded film |
MPa | ASTM D790 | |
落锤冲击 Drop hammer impact |
|||
40 µm,吹塑薄膜 40 µ m, blow molded film |
g | ASTM D1709 | |
埃尔曼多夫抗撕强度 Elmandorf tear strength |
ASTM D1922 | ||
MD:40 µm,吹塑薄膜 MD: 40 µ m, blow molded film |
g | ASTM D1922 | |
TD:40 µm,吹塑薄膜 TD: 40 µ m, blow molded film |
g | ASTM D1922 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
我国发布首份海洋能源发展报告
2022-01-22 搜料网资讯: 图为发布会现场。(赵亮 摄) 中国海油集团能源经济研究院1月14日发布《中国海洋能源发展报告2021》。这是我国首份全面、客观、专业地回顾和展望海洋能源发展的综合性 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |