牌号简介 About |
---|
Boltaron Rigiwall® 4333W是一种专利的压延丙烯酸/PVC合金板,设计为防紫外线、耐用、保护性墙面,用于露台外壳。Boltaron Rigiwall® 4333W提供1-A级建筑规范等级、卓越的冲击强度、耐磨性、耐污性和耐化学性。Boltaron 4333W的背面经过电晕处理,以提高粘附力。颜色:浅色仪表:.022至.040宽度:最长60英寸长度:最长120英寸自定义尺寸:根据要求纹理:哑光/哑光沙堡毛细胞抗刮擦耐磨 Boltaron Rigiwall® 4333W is a proprietary, calendered Acrylic/PVC Alloy sheet, designed as a UV resistant, durable, protective wall covering for patio enclosures. Boltaron Rigiwall® 4333W offers a class 1-A building code rating, excellent impact strength, abrasion resistance, and stain and chemical resistance. Boltaron 4333W is corona treated on the back side for improved adhesion. Colors: Light colors Gauges: .022 to .040 Widths: Up to 60" Lengths: Up to 120" Custom Sizes: Upon request Textures: Matte/Matte Sandcastle Haircell Scratch Resistant Abrasion Resistant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.37 | g/cm³ | ASTM D792 |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
水气透过率 Water vapor transmittance |
ASTM E96 | ||
PRO B PRO B |
0.0800 | US perms | ASTM E96 |
PRO BW PRO BW |
0.130 | US perms | ASTM E96 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
530 到 800 | J/m | ASTM D256 |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热老化 - Color Change L*a*b Heat Aging - Color Change L * a * b |
|||
70℃ 70℃ 2 |
0.400 | ||
70℃ 70℃ 3 |
|||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD MD |
1/℃ | ASTM D696 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
火焰传播 flame propagation |
ASTM E84 | ||
< 635.0 µm < 635.0 µm |
ASTM E84 | ||
< 736.6 µm < 736.6 µm |
ASTM E84 | ||
< 1.09 mm < 1.09 mm |
ASTM E84 | ||
< 1.63 mm < 1.63 mm |
ASTM E84 | ||
Smoke Developed Smoke Developed |
ASTM E84 | ||
< 635.0 µm < 635.0 µm |
ASTM E84 | ||
< 1.09 mm < 1.09 mm |
ASTM E84 | ||
< 1.63 mm < 1.63 mm |
ASTM E84 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
尺寸稳定性 dimensional stability |
|||
230℃,152.40 cm 230℃,152.40 cm |
% | ||
24 hr:70℃ 24 hr:70℃ |
% | ||
7 days:70℃ 7 days:70℃ |
% | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
泰伯耐磨性 Taber abraser |
|||
1000 周期,1000 g,CS-17 转轮 1000 cycles, 1000 g, CS-17 wheels |
mg | ASTM D1044 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 7 days |
3 24 hrs |
【新闻资讯】查看全部
日本CFC设计公司�Q定扩展 C/C复合资料的使用领域
2017-09-08 近年来与汽车用零件材料大厂的交易量增加,日本CFC设计公司决定扩大 C/C复合材料(碳素纤维强化碳素复合材料)的使用领域。相较于SUS(不锈钢)制的板材,C/C复合材料的重量可降到1/4以下,可大幅减少为了升温所产生的电力。 此外,积载于板材上的制品在1000℃的环境下使用数个月, SUS制板材会严重变形,C/C板材则是毫无变化;原本仅有2~3个月寿命的板材能使用5~10年,总成本的削减效果十分可观。该公司将以汽车领域为首,针对尚未采用C/C复合材料的顾客,主打治具的长寿化 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |