牌号简介 About |
---|
亚太地区不提供 CELEX 501.C is a high flow PC/ABS alloy. It combines the superior physical properties, high heat resistance of PC and the excellent processability of ABS. CELEX 501.C is designed for use in thin wall injection products and mobile phone housing. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.12 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
230℃,3.80kg 230℃,3.80kg |
8.3 | g/10min | ASTM D1238 |
250℃,5.0kg 250℃,5.0kg |
30 | g/10min | ASTM D1238 |
260℃,5.0kg 260℃,5.0kg |
36 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD:3.2 mm MD:3.2 mm |
0.40 到 0.60 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服,3.20 mm Yield, 3.20 mm |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
|||
3.20 mm 3.20 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
3.20 mm 3.20 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
0.80 mm 0.80 mm 2 |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 这个额定值并非为了反映这种或任何其他材料在实际起火条件下造成的危险。 |
【新闻资讯】查看全部
陶氏Enerlyte聚氨酯弹性体用于鞋底
2018-07-03 意大利Porto Recatini――Mondial Suole公司选用了陶氏的Enerlyte聚氨酯弹性体,用以制作其iTen系列产品的鞋底,这款鞋针对运动休闲鞋市场。 Mondial Suole公司成立于1978年,位于意大利亚得里亚海沿。公司选用陶氏的Enerlyte聚氨酯弹性体是基于其柔软的触感和耐用性。 陶氏补充道,鞋底的材料是用水发泡的,使其对于其他的鞋底材料更加环境友善。 陶氏化学说,这种材料具有的成分和形态,使客户能够开发舒适 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |