牌号简介 About |
---|
Infino SA-1100是一种聚碳酸酯(PC)产品,。 它,在北美洲、非洲和中东、拉丁美洲、欧洲或亚太地区有供货。 主要特性为:阻燃/额定火焰。 Infino SA-1100 is a Polycarbonate (PC) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Electrical/Electronic Applications. Primary characteristic: flame rated. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
|||
- - |
1.20 | g/cm³ | ISO 1183 |
|
1.20 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
9.0 | g/10min | ISO 1133 |
300℃,1.20kg 300℃,1.20kg |
9.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
ISO 2577 | ||
TD:3.2 mm TD:3.2 mm |
0.48 to 0.58 | % | ASTM D955 |
MD:3.2 mm MD:3.2 mm |
% | ASTM D955 | |
TD:3.2 mm TD:3.2 mm |
% | ISO 2577 | |
MD:3.2 mm MD:3.2 mm |
% | ISO 2577 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength 5 |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃ 23℃ 5 |
kJ/m² | ISO 180-1A | |
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,6.4 mm 1.8 MPa, unannealed, 6.4 mm |
℃ | ASTM D648 | |
1.8 MPa,未退火,4.0 mm 1.8 MPa, unannealed, 4.0 mm |
℃ | ISO 75-2/A | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
|||
1.50-3.00 mm 1.50-3.00 mm |
UL 94 | ||
灼热丝起燃温度 Igniting temperature of the hot wire |
|||
1.5 mm 1.5 mm |
℃ | IEC 60695-2-13 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
断裂 fracture |
MPa | ISO 527-2/50 | |
断裂 fracture 2 |
MPa | ASTM D638 | |
屈服 yield 2 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture |
% | ISO 527-2/50 | |
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
MPa | ASTM D790 | |
弯曲模量 Bending modulus 4 |
MPa | ISO 178 | |
弯曲强度 bending strength 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
MPa | ISO 178 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ISO 2039-2 | ||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 0.11 in/min |
4 0.079 in/min |
5 Thickness: 4mm |
【新闻资讯】查看全部
医用塑料论坛预告[一]:PEEK和合金资料的共同优势
2016-03-18 2016国际橡塑展期间举行的【第二届医用塑料论坛】邀请了多名国际性医用塑料专家为大家分享医疗级聚合物的最新应用和前沿生产技术。今次要介绍的议题是PEEK和合金材料的独特优势。 PEEK(聚醚醚酮)树脂是目前热塑性树脂中综合性能最优异的一类。由于具有优良的生物相容性,接近人骨的弹性模量,X光下的可透视性等独特性能, PEEK在医疗领域得到了越来越广泛的应用。 致力于医用塑料制品研制的天津市塑料研究所有限公司,将对PEEK的基本特性以及其在医疗植入领域所具有的独 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |