牌号简介 About |
---|
Innomid CS 6-9000是一种未填充的聚酰胺(PA-6)化合物。该等级有自然色和定制色两种形式。推荐应用Innomid CS 6-9000用于生产注塑产品,要求的性能是高强度和刚度。 Taitalac® 6000H is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for extrusion. Important attributes of Taitalac® 6000H are: Flame Rated Impact Resistant Typical applications include: Business/Office Goods Consumer Goods |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.04 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
ASTM D1238 | ||
200℃,5.0kg 200℃,5.0kg |
0.50 | g/10min | ASTM D1238 |
220℃,10.0kg 220℃,10.0kg |
5.5 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
< 0.40 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
24hr 24hr |
< 0.30 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
23℃,3.2mm 23℃,3.2mm |
J/m | ASTM D256 | |
23℃,6.4mm 23℃,6.4mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,12.7 mm 1.8 MPa, unannealed, 12.7 mm |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 4 | |
相对温度指数 Relative temperature index |
|||
电气性能,1.60 mm Electrical performance, 1.60 mm |
℃ | UL 746 | |
强度机械性能,1.60 mm Strength mechanical performance, 1.60 mm |
℃ | UL 746 | |
冲击机械性能,1.60 mm Impact mechanical performance, 1.60 mm |
℃ | UL 746 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
高电弧燃烧指数(HAI)(1.57 mm) High Arc Burning Index (HAI) (1.57 mm) |
UL 746 | ||
高电压电弧起痕速率(HVTR)(1.57 mm) High voltage arc marking rate (HVTR) (1.57 mm) |
mm/min | UL 746 | |
热丝引燃(HWI)(1.57 mm) Hot wire ignition (HWI) (1.57 mm) |
sec | UL 746 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.60 mm 1.60 mm |
UL 94 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength 2 |
|||
断裂,23℃,3.18 mm Fracture, 23 ℃, 3.18 mm 2 |
MPa | ASTM D638 | |
屈服,23℃,3.18 mm Yield, 23 ℃, 3.18 mm 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂,23℃,3.18 mm Fracture, 23 ℃, 3.18 mm 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 3 |
|||
23℃ 23℃ 3 |
MPa | ASTM D790 | |
弯曲强度 bending strength 4 |
|||
屈服,23℃ Yield, 23 ℃ 4 |
MPa | ASTM D790 | |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 类型1A, 0.079 in/min |
【新闻资讯】查看全部
中博会进行时 | 当拓斯达遇见“小蛮腰”
2021-09-17 搜料网资讯: 9月16日,第十七届中国国际中小企业博览会(下称中博会)在广州开幕。 拓斯达作为东莞智能制造代表企业之一,携CNC(数控机床)和机器人两大产品亮相 ,首次展示其 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |