牌号简介 About |
---|
ES6004是为吹塑段设计的高密度聚乙烯均聚物。ES6004具有较高的刚度特性、良好的抗冲击性和良好的表面质量。用途:吹塑小体积:润滑油、食用油、牛奶、果汁、酸奶瓶;玩具。工艺:吹塑。 ES6004 is a high density polyethylene, homopolymer designed for the blow-molding segment. ES6004 shows high stiffness properties, good impact resistance and good surface quality. Applications: Blow Molded Small Volume: Bottles for lubricant and edible oils, milk, juice and yogurt; Toys. Process: Blow Molding. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.960 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
190℃,21.6kg 190℃,21.6kg |
30 | g/10min | ASTM D1238 |
190℃,2.16kg 190℃,2.16kg |
0.35 | g/10min | ASTM D1238 |
抗环境应力开裂 ESCR(Environmental Stress Cracking Resistance) |
|||
2.00 mm,100% 2.00 mm,100% |
29 | hr | ASTM D1693 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
70 | ℃ | ASTM D648 |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ASTM D2240 | ||
拉伸强度 tensile strength |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
万华化学2018年报,完成净利润106.10亿元,同比下降了4.17%??
2019-04-24 3月万华化学宣布延迟2018年度报告的发布。 4月22日晚万华发布了2018年年报,公司2018年实现营业 总收入606.2亿,同比增长14.11%;实现归属于母公司所有者的净利润106.1亿,同比下降4.71%; |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |