牌号简介 About |
---|
VIPEL F086系列是一种溶于苯乙烯的环氧酚醛乙烯基酯树脂,设计用于耐高温。F066系列非常适合用于手工铺层、喷漆和纤维缠绕工艺,其中突出的机械性能和耐化学品、氧化和热是必需的。优点耐腐蚀性VIPEL F086是专为耐高温设计的。环氧树脂-酚醛树脂骨架具有耐酸性,对许多有机溶剂具有优异的耐性。Vipel F086系列通常比标准双酚A环氧乙烯基酯树脂或标准酚醛树脂更耐液体和蒸汽。请参阅AOC的“耐腐蚀树脂指南”,了解耐腐蚀信息或关于树脂是否适合任何特定化学环境的问题。机械性能F086系列适用于经受特别高温应用的模具。适用于各种制造方法,如手捻、长丝缠绕等。适用于各种制造方法,如手捻、长丝缠绕等。 The Vipel F086 series is an epoxy novolac vinyl ester resin dissolved in styrene and designed for high temperature resistance. F086 series is ideally suited for use in hand lay-up, spray-up, and filament winding processes where outstanding mechanical properties and resistance to chemicals, oxidation and heat are required. BENEFITS Corrosion Resistance Vipel F086 is designed for high temperature resistance. The epoxy novolac backbone provides resistance to acids and has superior resistance to many organic solvents. Vipel F086 series is generally resistant to liquids and vapors at higher temperatures than standard bisphenol-A epoxy vinyl ester resins or standard novolacs. Refer to AOC's "Corrosion Resistant Resin Guide" for corrosion resistance information or for questions regarding suitability of a resin to any particular chemical environment contact AOC. Mechanical Properties The F086 series is suitable for moldings that are subjected to particularly high temperature applications. Suitable for various fabricating methods such as hand lay-up, filament winding, etc. Versatile Suitable for various fabricating methods such as hand lay-up, filament winding, etc. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
苯乙烯含量 styrene content |
37 | % | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
166 | ℃ | ASTM D648 |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
Gel to Peak Gel to Peak |
15.0 | min | |
放热峰值 exothermic peak |
199 | ℃ | |
Uncured Properties Uncured Properties |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.08 | g/cm³ | |
粘度 viscosity |
|||
布络克菲尔德 RVT,25℃ 25℃,Brookfield RVT |
Pa·s | ||
胶凝时间 Gelation time |
|||
25℃ 25℃ |
min | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
巴氏硬度 Babbitt hardness |
ASTM D2583 | ||
拉伸模量 Tensile modulus |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |