牌号简介 About |
---|
TPX® MX004 TPX® MX004是一种聚甲基戊烯共聚物(PMP 共聚物)材料,。 该产品在北美洲有供货,加工方式为:吹塑成型、管路挤出成型、挤出、纤维(纺纱)挤出、型材挤出成型或注射成型。 TPX® MX004的主要特性为:良好的刚度。 TPX® MX004 TPX® MX004是一种聚甲基戊烯共聚物(PMP 共聚物)材料,。 该产品在欧洲或亚太地区有供货,加工方式为:挤出或注射成型。 TPX® MX004的主要特性为:坚硬。 TPX® MX004的典型应用领域为:食品接触应用 TPX™ MX004 TPX™ MX004 is a Polymethylpentene Copolymer (PMP Copolymer) material. It is available in North America for blow molding, extrusion, fiber (spinning) extrusion, injection molding, pipe extrusion, or profile extrusion. Primary attribute of TPX™ MX004: Good Stiffness. TPX™ MX004 TPX™ is a 4-methylpentene-1-based olefin copolymer. TPX™ has a unique molecular structure. Although TPX™ is a crystalline olefin polymer, it shows transparency. Because of its excellent heat-resistance, release property and chemical resistance, TPX™ is used for industrial materials, including mandrels and sheaths in the manufacture of high-pressure rubber hose, mold cups to create LED light and other applications such as release film on FPC manufacturing process and release paper in the manufacture of synthetic leather. Furthermore, TPX™ possesses a lowest density among thermoplastic polymers and then provides the molded articles with lower weight. This leads to reduce the environmental load for transportation. It is also noted that TPX™ is a halogen-free polymer denoted as environmentally-friendly material. TPX™ is also used for food-related applications such as food wraps, food preservation packs, baking carton and microwave oven tableware. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.833 | g/cm³ | 内部方法 |
熔体质量流动速率 Melt Flow Rate |
|||
260℃,5.0kg 260℃,5.0kg |
25 | g/10min | 内部方法 |
螺旋流动长度 Spiral flow length 3 |
53.0 | cm | 内部方法 |
收缩率 Shrinkage rate 4 |
内部方法 | ||
MD:2.0 mm MD:2.0 mm |
1.7 | % | 内部方法 |
TD:2.0 mm TD:2.0 mm |
1.4 | % | 内部方法 |
吸水率 Water absorption rate |
|||
饱和 saturated |
% | ASTM D570 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
注塑 Injection molding |
J/m | ASTM D256 | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃,注塑成型 23 ℃, injection molding |
J/m | ASTM D4812 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature 7 |
|||
0.45 MPa,未退火,6.35 mm 0.45 MPa, unannealed, 6.35 mm 7 |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 8 | |
结晶峰温度 Crystallization peak temperature |
|||
DSC DSC |
℃ | ASTM D3418 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-10~160℃ MD:-10~160℃ |
1/℃ | 内部方法 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity 9 |
|||
2 mm 2 mm 9 |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength 9 |
|||
2 mm 2 mm 9 |
kV/mm | ASTM D149 | |
介电常数 Dielectric constant 9 |
|||
2.00 mm,1 MHz 2.00 mm,1 MHz 9 |
ASTM D150 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index 10 |
ASTM D542 | ||
透光率 Transmittance |
|||
注塑成型 injection molding |
% | ASTM D1003 | |
雾度 Haze |
|||
注塑薄膜 Injection molded film |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus 5 |
|||
23℃,注塑成型 23 ℃, injection molding 5 |
MPa | ASTM D638 | |
拉伸强度 tensile strength 5 |
ASTM D638 | ||
屈服,23℃,注塑成型 Yield, 23 ℃, injection molding |
MPa | ASTM D638 | |
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 5 |
|||
断裂,23℃,注塑成型 Fracture, 23 ℃, injection molding 5 |
% | ASTM D638 | |
弯曲模量 Bending modulus 6 |
|||
3.20 mm,注塑成型,51 mm跨距 3.20 mm, injection molded, 51 mm span 6 |
MPa | ASTM D790 | |
弯曲强度 bending strength 6 |
|||
3.20 mm,注塑成型,51 mm跨度 3.20 mm, injection molded, 51 mm span 6 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 模具温度: 163°F, 熔体温度: 590°F |
3 260 to 280°C |
4 类型 4, 2.0 in/min |
5 0.051 in/min |
6 120°C/hr |
7 速率 A (50°C/h), 压 力1 (10N) |
8 Injection Molded |
9 Injection Molded, 2 mm, 589 nm wavelength |
【新闻资讯】查看全部
美银高盛齐唱多!原油价格可能在年底或明年达到每桶100美元
2021-06-22 搜料网资讯: 华尔街越来越普遍的共识是,随着全球经济从新冠肺炎疫情中复苏,油价上涨还有更大的上行空间,可能会大幅上涨。 美国银行(Bank Of America)的大宗商品策略师弗朗西斯 |
美银高盛齐唱多!原油价格可能在年底或明年达到每桶100美元 搜料网资讯:华尔街越来越普遍的共识是,随着全球经济从新冠肺炎疫情中复苏,油价上涨还有更大的上行空间,可能会大幅上涨。 美国银行(Bank Of America)的大宗商品策略师弗朗西斯科·布兰奇(Francisco Blanch)周一在一份研究报告中表示,他认为明年油价有理由将可达到每桶100美元。 “首先,在18个月的封锁之后,有大量被压抑的流动需求。其次,公共交通将滞后,在很长一段时间内促进私家车的使用。第三,大流行之前的研究表明,随着在家工作转变为开车上班,更多的远程工作可能会导致更多的驾车里程。在供应方面,我们预计美国和世界各地的政府政策压力将在未来几个季度遏制资本支出,以实现巴黎减排目标。其次,出于财务和ESG原因,投资者对能源行业支出的反对声音变得更加强烈。第三,限制二氧化碳排放的司法压力正在上升。简而言之,需求势将反弹,供应可能无法完全跟上,这将使欧佩克在2022年对原油市场加以控制。”布兰奇解释道。 尽管木材和铜等其他大宗商品价格最近有所回调,但油价仍保持看涨倾向。 国际布伦特原油期货价格目前在每桶74.63美元以上,交易水平为2018年秋季以来未曾见过的水平。在过去一年时间里,布伦特原油期货价格累计上涨了88%左右。 在经济反弹满足低供应水平的情况下,有迹象表明需求强劲,这推动了最近油价的上涨势头。 美国能源情报署(EIA)上周报告称,截至6月11日的一周,美国原油库存减少了740万桶。与此同时,国家统计局(National Bureau Of Statistics)报告称,中国5月份原油吞吐量同比增长4.4%,创历史新高。 与美国银行类似,高盛集团(Goldman Sachs)也预计油价将进一步走强。这家投行的策略师表示,不排除油价在年底前接近每桶100美元的可能性。 高盛集团的大宗商品研究全球主管杰弗里·柯里(Jeffrey Currie)认为,最近几天以来,随着美国将“接力棒”传递给欧洲和新兴市场,全球需求可能从几周前的每天9500万桶上升到9700万桶。他指出:“短期内,我们最有信心的市场是石油。我们认为布伦特原油今年第三季度的平均价格将可达到每桶80美元,潜在涨幅远高于每桶80美元。随着美国将接力棒传递给欧洲和新兴市场,就连印度也开始在这些市场上显示出改善。” 柯里补充说:“除了核心的OPEC+之外,石油需求增长如此强劲,而供应曲线几乎没有弹性,因此全球石油市场正面临自去年夏天以来最严重的缺口,达到了每天近300万桶。随着炼油商对利润率的小幅改善迅速做出反应,石油产品供应与最终用户需求的跃升大体相当,这一缺口几乎全部是原油。” 由于市场对夏季需求强劲的前景抱有希望,再加上强硬派人士赢得了伊朗总统大选后,油价周一大幅上涨。澳新银行(ANZ)分析师表示,易卜拉欣·莱希(Ebrahim Raisi)在伊朗选举中获胜,这可能会推迟核协议的达成。他们在一份报告中写道:“伊朗石油在短期内冲击市场的可能性看起来不大。” 由于强劲的需求预期,今年到目前为止,美国西德克萨斯轻质原油(WTI)期货价格和国际布伦特原油期货价格都已经累计上涨了40%以上。澳新银行表示:“北半球夏季需求的反弹如此强劲,以至于市场越来越担心库存将进一步大幅减少。” |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
抱歉!该牌号暂无认证数据。
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。