CALIBRE™ MEGARAD 2081-10 聚碳酸酯树脂的原色近于水清色的外观,适用于辐射灭菌医疗器具的最终用户的应用。与通用型的聚碳酸酯树脂相比,在高能辐射能量(伽马线或者电子束)的辐射下,CALIBRE MEGARAD 2081-10 树脂的颜色变化要低50%。CALIBRE 2081-10 树脂应经根据ISO 10993 (医疗器械生物学评价)的要求进行过测试,适合用于获准的医疗应用领域。该产品含有脱模剂。 主要特性 ISO 10993 应用领域: 医疗应用领域 CALIBRE™ MEGARAD 2081-10 Polycarbonate resin provides end-users of radiation sterilized medical devices a color closer to the water-clear look of the natural resin. When exposed to high energy radiation (gamma or electron beam), CALIBRE MEGARAD 2081-10 resin can reduce the color shift by 50% compared to general purpose polycarbonate resins. CALIBRE 2081-10 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. Main Characteristics Stabilized for high energy radiation Tested under ISO 10993 Transparent Contains mold release Applications: Medical applications |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.20 | g/cm³ | ASTM D792 , ISO 1183/A |
熔体质量流动速率 Melt Flow Rate |
|||
300℃,1.20kg 300℃,1.20kg |
10 | g/10min | ASTM D1238,ISO 1133 |
收缩率 Shrinkage rate |
|||
MD MD |
0.50 到 0.70 | % | ASTM D955 |
MD MD |
0.50 到 0.70 | % | ISO 294-4 |
吸水率 Water absorption rate |
ASTM D570 , ISO 62 | ||
23℃,24hr 23℃,24hr |
0.15 | % | ASTM D570,ISO 62 |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ASTM D570,ISO 62 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
kJ/m² | ISO 180-A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
|||
23℃ 23℃ |
ASTM D256 , ISO 180 | ||
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments 7 |
|||
23℃,总能量 23 ℃, total energy 7 |
J | ASTM D3763 | |
拉伸冲击强度 Tensile impact strength |
kJ/m² | ASTM D1822 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,退火 0.45 MPa, annealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
1.8 MPa,退火 1.8 MPa, annealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ASTM D1525 | |
B50 B50 |
℃ | ISO 306 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
MD:-40~82℃ MD:-40~82℃ |
1/℃ | ASTM D696 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ohms·cm | ASTM D257 | |
介电强度 Dielectric strength |
kV/mm | ASTM D149,IEC 60243-1 | |
介电常数 Dielectric constant |
ASTM D150 | ||
60 Hz 60 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
耗散因数 Dissipation factor |
ASTM D150 | ||
50 Hz 50 Hz |
ASTM D150 | ||
1 MHz 1 MHz |
ASTM D150 | ||
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
折射率 Refractive index |
ASTM D542 , ISO 489 | ||
透光率 Transmittance |
% | ASTM D1003 | |
雾度 Haze |
% | ASTM D1003 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
ASTM D785 | ||
M 级 M-level |
ASTM D785 | ||
R 级 R-level |
ASTM D785 | ||
拉伸模量 Tensile modulus |
|||
-- -- 3 |
MPa | ASTM D638 | |
-- -- |
MPa | ISO 527-2/50 | |
拉伸强度 tensile strength |
|||
屈服 yield 3 |
MPa | ASTM D638 | |
屈服 yield |
MPa | ISO 527-2/50 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
断裂 fracture |
MPa | ISO 527-2/50 | |
拉伸应变 Tensile strain |
|||
屈服 yield 3 |
% | ASTM D638 | |
屈服 yield |
% | ISO 527-2/50 | |
断裂 fracture 3 |
% | ASTM D638 | |
断裂 fracture |
% | ISO 527-2/50 | |
弯曲模量 Bending modulus |
|||
-- -- 4 |
MPa | ASTM D790 | |
-- -- 5 , 6 |
MPa | ISO 178 | |
弯曲强度 bending strength |
|||
-- -- 4 |
MPa | ASTM D790 | |
-- -- 5 , 6 |
MPa | ISO 178 | |
耐磨耗性 Wear resistance |
% | ASTM D1044 |
备注 |
---|
1 Biocompatibility testing following ISO Guidelines 10993 has been completed on select classic resins in this series. Please consult Styron for details. ISO guidelines include a sensitization test. |
2 一般属性:这些不能被视为规格。 |
3 2.0 in/min |
4 方法 I (三点负荷), 0.079 in/min |
5 0.079 in/min |
6 3 点 |
7 11.1 ft/sec |
【新闻资讯】查看全部
江苏冠军集团2021年中总结大会圆满召开
2021-07-11 搜料网资讯: 7月2日上午,冠军集团营销中心全体人员在运营大楼三楼营销中心会议室召开了2021年中总结大会。会上,董事长谢海先生听取了销售总监刘其飞、运营总监任贤萍的详细工 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |