牌号简介 About |
---|
LNP™ THERMOCOMP™ 2X04505是一种基于ETFE树脂的化合物,含有专有填料。 LNP THERMOCOMP 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s). |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.75 | g/cm³ | ASTM D792 |
密度 Density |
1.74 | g/cm³ | ISO 1183 |
收缩率 Shrinkage rate |
ISO 294-4 | ||
TD:24 hrs TD:24 hrs |
1.8 to 2.0 | % | ASTM D955 |
MD:24 hrs MD:24 hrs |
1.0 to 1.2 | % | ASTM D955 |
TD:24 hrs TD:24 hrs |
1.9 | % | ISO 294-4 |
MD:24 hrs MD:24 hrs |
% | ISO 294-4 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus 2 |
MPa | ASTM D638 | |
拉伸模量 Tensile modulus |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂 fracture |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ISO 527-2 | |
屈服 yield |
MPa | ASTM D638 | |
屈服 yield |
MPa | ASTM D638 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂 fracture |
MPa | ASTM D638 | |
断裂 fracture 3 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
屈服 yield |
% | ASTM D638 | |
屈服 yield |
% | ASTM D638 | |
拉伸应变 Tensile strain |
ASTM D638 | ||
断裂 fracture |
% | ISO 527-2 | |
屈服 yield |
% | ISO 527-2 | |
断裂 fracture |
% | ASTM D638 | |
断裂 fracture 3 |
% | ASTM D638 | |
弯曲模量 Bending modulus |
ASTM D790 | ||
50 mm跨距 50 mm span 4 |
MPa | ASTM D790 | |
-- -- |
MPa | ASTM D790 | |
弯曲模量 Bending modulus |
MPa | ISO 178 | |
弯曲强度 bending strength |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch 5 |
|||
23℃ 23℃ |
J/m | ASTM D4812 | |
23℃ 23℃ |
J/m | ASTM D256 | |
23℃ 23℃ 5 |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam 5 |
|||
23℃ 23℃ 5 |
kJ/m² | ISO 180/1U | |
装有测量仪表的落镖冲击 Dart impact equipped with measuring instruments |
|||
23℃,Energy at Peak Load 23℃,Energy at Peak Load |
J | ASTM D3763 | |
多轴向仪器化冲击能量 Multi axial instrumented impact energy |
J | ISO 6603-2 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,64 mm跨距 1.8 MPa, unannealed, 64 mm span 6 |
℃ | ISO 75-2/Af | |
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,64 mm跨距 0.45 MPa, unannealed, 64 mm span 6 |
℃ | ISO 75-2/Bf | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ISO 11359-2 | |
TD:-40~40℃ TD:-40~40℃ |
1/℃ | ASTM E831 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ISO 11359-2 | |
MD:-40~40℃ MD:-40~40℃ |
1/℃ | ASTM E831 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
3 类型 1, 0.20 in/min |
4 0.051 in/min |
5 80*10*4 |
6 80*10*4 mm |
【新闻资讯】查看全部
国内聚丙烯次要来源的利润亦是增长分明利好市场
2018-08-01 虽目前处于需求淡季,但国内聚丙烯粒料市场不乏利好支撑。首先,国际原油高位支撑塑料市场。其次,装置检修高峰、社会库存回落供应端偏紧,而近期人民币贬值,出口窗口打开,需求端缓解,市场供需格局好转再度支撑市场。而市场重心持续走高后,国内聚丙烯主要来源的利润亦是增长明显利好市场。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |