它是热塑性弹性体(TPE)系列中的一种软质、可着色、非吸湿性热塑性硫化弹性 体(TPV)。这种材料同时具有良好的物理性质和耐化学性,适用于广泛的领域。 这一牌号的山都平 TPV 是剪切速率依赖型产品,可在常规热塑性注塑成型、挤出 成型、吹塑成型、热成型或真空成型设备上加工。这是一种聚烯烃基材料,可在生 产过程中进行回收利用。 A soft, colorable, non-hygroscopic thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding, extrusion, blow molding, thermoforming or vacuum forming. It is polyolefin based and recyclable within the manufacturing stream. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.948 | g/cm³ | ASTM D792 |
密度 Density |
0.950 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
9.80 | MPa | ASTM D412 |
TD,断裂,23℃ TD, fracture, 23 ℃ |
9.80 | MPa | ISO 37 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
4.20 | MPa | ASTM D412 |
TD,100% 应变,23℃ TD, 100% strain, 23 ℃ |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
|||
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ASTM D412 | |
TD,断裂,23℃ TD, fracture, 23 ℃ |
% | ISO 37 | |
撕裂强度 tear strength |
|||
TD,23℃ TD,23℃ |
kN/m | ISO 34-1 | |
TD,23℃ TD,23℃ |
kN/m | ASTM D624 | |
压缩形变 Compression deformation |
ASTM D395B | ||
70℃,22 hr 70℃,22 hr |
% | ASTM D395B | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395B | |
压缩形变 Compression deformation |
ISO 815 | ||
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 A,15 秒,23℃ Shore A, 15 seconds, 23 ℃ |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
脆化温度 Embrittlement temperature |
℃ | ASTM D746 | |
脆化温度 Embrittlement temperature |
℃ | ISO 812 | |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
UL 746 | ||
1.1 mm 1.1 mm |
℃ | UL 746 | |
1.6 mm 1.6 mm |
℃ | UL 746 | |
3.0 mm 3.0 mm |
℃ | UL 746 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 The rate of change in tensile strength in air |
|||
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
空气中极限伸长率的变化率 The rate of change in ultimate elongation in air |
|||
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
Change in Tensile Strain at Break in Air(150℃,168 hr) Change in Tensile Strain at Break in Air(150℃,168 hr) |
% | ISO 188 | |
Change in Durometer Hardness in Air(邵氏 A,150℃,168 hr) Change in Durometer Hardness in Air (150 ℃, 168 hr) |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
|||
邵氏 A,150℃,168 hr Shaw A, 150 ℃, 168 hr |
ISO 188 | ||
Change in Mass in Air(150℃,168 hr) Change in Mass in Air(150℃,168 hr) |
% | ASTM D573 | |
Change in Mass in Air(150℃,168 hr) Change in Mass in Air(150℃,168 hr) |
% | ISO 188 | |
拉伸强度的变化率 The rate of change in tensile strength |
ASTM D471 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
拉伸强度的变化率 The rate of change in tensile strength |
ISO 1817 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
极限伸长率的变化率 Change rate of ultimate elongation |
ASTM D471 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
断裂时拉伸应力变化 Changes in tensile stress during fracture |
ISO 1817 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ISO 1817 | |
邵氏硬度的变化率 The rate of change in Shore hardness |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氯化钠中,15% Shore A, 23 ℃, 168 hr, in sodium chloride, 15% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在硫酸中,98% Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% |
ASTM D471 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ASTM D471 | ||
邵氏硬度的变化率 The rate of change in Shore hardness |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在IRM 903 油中 Shaw A, 23 ℃, 168 hr, in IRM 903 oil |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氯化钠中,15% Shore A, 23 ℃, 168 hr, in sodium chloride, 15% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在氢氧化钠中,50% Shore A, 23 ℃, 168 hr, in sodium hydroxide, 50% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在硫酸中,98% Shore A, 23 ℃, 168 hr, in sulfuric acid, 98% |
ISO 1817 | ||
邵氏 A,23℃,168 hr,在水中 Shaw A, 23 ℃, 168 hr, in water |
ISO 1817 | ||
质量变化率 Quality change rate |
ASTM D471 | ||
23℃,168 hr,in IRM 903 Oil 23℃,168 hr,in IRM 903 Oil |
% | ASTM D471 | |
23℃,168 hr,in Sodium Chloride,15% 23℃,168 hr,in Sodium Chloride,15% |
% | ASTM D471 | |
23℃,168 hr,in Sodium Hydroxide,50% 23℃,168 hr,in Sodium Hydroxide,50% |
% | ASTM D471 | |
23℃,168 hr,in Sulfuric Acid,98% 23℃,168 hr,in Sulfuric Acid,98% |
% | ASTM D471 | |
23℃,168 hr,在水中 23 ℃, 168 hr, in water |
% | ASTM D471 | |
质量变化率 Quality change rate |
ISO 1817 | ||
23.0℃,168 hr,in Sodium Chloride,15% 23.0℃,168 hr,in Sodium Chloride,15% |
% | ISO 1817 | |
23.0℃,168 hr,in Sodium Hydroxide,50% 23.0℃,168 hr,in Sodium Hydroxide,50% |
% | ISO 1817 | |
23.0℃,168 hr,in Sulfuric Acid,98% 23.0℃,168 hr,in Sulfuric Acid,98% |
% | ISO 1817 | |
23.0℃,168 hr,in Water 23.0℃,168 hr,in Water |
% | ISO 1817 | |
23.0℃,168 hr,in IRM 903 Oil 23.0℃,168 hr,in IRM 903 Oil |
% | ISO 1817 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
体积电阻率 Volume resistivity |
ASTM D257 | ||
23 ℃,2.0 mm 23 ℃,2.0 mm |
ohms·cm | ASTM D257 | |
23 ℃,3.20 mm 23 ℃,3.20 mm |
ohms·cm | ASTM D257 | |
相比漏电起痕指数 Compared to the leakage tracing index |
UL 746 | ||
高电弧燃烧指数(HAI) High Arc Burning Index (HAI) |
UL 746 | ||
高压电弧抗点燃指数(HVAR)(PLC) High voltage arc ignition resistance index (HVAR) (PLC) |
UL 746 | ||
热丝引燃 Hot wire ignition |
|||
HWI HWI |
UL 746 | ||
1.6 mm 1.6 mm |
UL 746 | ||
3.0 mm 3.0 mm |
UL 746 | ||
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.10 mm 1.10 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.00 mm 3.00 mm |
UL 94 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 C 模具 |
3 B 方法,直角形试样(割口) |
4 类型 1 |
5 类型 A |
【新闻资讯】查看全部
292亿!美的拟成库卡最大股东
2016-05-23 18日下午,美的集团发布公告宣布,公司拟通过全资境外子公司向德国库卡集团股东发起收购要约,初步确定要约价格为每股115欧元,预计公司最高将支付不超过40亿欧元(折合人民币约292亿元)的现金对价。 目前美的集团已经间接持有库卡集团约13.5%股份,公司意图获得超过库卡集团30%以上的股份,成为库卡集团最大股东。美的承诺全力保持库卡的独立性及德国上市公司的地位。 |
292亿!美的拟成库卡最大股东 18日中午,美的集团发布消息公布,企业拟根据国有独资海外分公司向德国库卡集团公司公司股东进行回收质权,基本明确质权价钱为每一股115英镑,预估企业最大将付款不超过40亿英镑(折算rmb约292亿人民币)的现钱溢价增资。 现阶段美的集团早已间接性拥有库卡集团公司约13.5%股权,企业用意得到超出库卡集团公司30%之上的股权,变成库卡集团公司较大 公司股东。美的服务承诺全力以赴维持库卡的自觉性及德国上市企业的影响力。 美的拟将库卡公司股东进行回收质权,用意得到库卡30%之上的股权,变成较大 公司股东 针对本次回收,美的集团老总方洪波称,“美的沒有要签订标准协议或暂停上市的意向。美的提升对库卡的持仓占比,能够既维持库卡的自觉性,又能使俩家企业根据协作进一步驱动器提高,特别是在在中国销售市场。” 库卡集团公司是全世界领跑的智能机器人及自动化生产机器设备和解决方法的经销商之一。集团旗下现有库卡智能机器人、库卡系统软件和瑞仕格三个关键业务流程版块。2015年库卡集团公司完成主营业务收入29.66亿英镑,完成息稅前纯利润1.36亿英镑。企业资产总额为7.33亿英镑。依据IFR2015年的数据信息,在汽车工业行业,库卡智能机器人的市场占有率在全世界和欧州全是第一;在一般工业生产行业智能机器人的市场占有率在欧州列前三名;在系统软件解决方法的市场占有率英国排名第一,欧州排行第二。 美的悄悄地变成智能机器人大佬
2015年美的就拥有德国库卡个股5.43%,2020年2月,美的集团将其拥有的库卡股权占比提升至10.2%,变成该企业的第二控股股东。依照最新公告信息内容,美的集团间接性有着库卡13.5%的股份。 特别注意的是,除开全新进行的要约收购德国库卡,近些年,美的集团在智能机器人行业姿势持续。2015年8月4日,美的宣布公布与日本株式安川电机集团旗下分公司安川电机(中国)有限责任公司在板式办公家具创立俩家合资企业机器人厂家,各自承担工业机械手、智能机器人的研产供销。 除此之外,美的集团还入股埃夫特。据公布材料显示信息,埃夫特于2016年1月29日产生公司变更,现阶段其“公司股东情况”一栏显示信息,美的集团持仓17.8%,是企业第三控股股东。埃夫特是一家潜心从业工业生产机器人设计、产品研发、生产制造与系统应用,自动化技术武器装备设计方案与生产制造的高新科技公司。 除开埃夫特,德国库卡、日本安川都位居全球四大机器人厂家队伍。全球四大智能机器人大家族此外俩家为ABB集团公司和日本国发那科。 借以解决人力资本成本费增涨和智能制造系统
在对德国库卡要约收购的公示中,美的集团描述称,库卡关键战略布局之一是发展中国宽阔的智能机器人销售市场。 美的集团觉得中国人力资本成本费的持续升高和人口老化的状况,使智能机器人销售市场具备巨大的提高室内空间。中国有着世界最大的、产业链范畴最普遍的“一般工业生产”。做为传统式的劳动密集领域,家电业人力成本占较为大。为解决人力资本成本费增涨,美的从2015年逐渐,方案5年上用50亿人民币将生产流水线更新改造,逐渐减少人力应用水平。库卡亦表明,由于中国智能机器人销售市场宽阔,方案于2020年将中国销售市场的销售总额由以往财年的4.25亿英镑,提升至十亿英镑。 据机器人行业调查报告显示信息,中国汽车制造业的自动化技术占比做到了50%上下,而3C类(包含家用电器)却仅有14%,家电业智能机器人的提高室内空间较为大。 美的集团2015年财务报告显示信息,汇报期限内,美的集团完成主营业务收入1384亿人民币,环比微跌2.28%;归总公司纯利润127亿人民币,同比增长率21%;生产经营造成的现金流净收益268亿人民币。 加速国际性合理布局,美的本年度销售业绩总体目标为250亿英镑
两月以前,美的集团刚发布了拟以4.73亿美金回收日本东芝家用电器业务流程行为主体“飞利浦生活家电注解会社”80.1%股份的信息,该收购计划预估在2020年6月进行。 据统计,2015年,美的进行智能家居 智能制造系统“双智”发展战略,不仅通过项目投资于智能机器人提高美的的生产制造及物流自动化,也科学研究开发设计以自动化技术为基本的智能家居系统机器设备。美的的总体目标是,将来多年将总体销售总额提高至超出250亿英镑,在其中智能产品及智能机器人会为销售总额提高产生卓越贡献。 以往的2015年,美的集团在与国外资产和技术性、销售市场相关的合理布局也多有姿势。2015年3月,美的集团和德国BOSCH公布,在美的合肥市生产制造产业基地生产制造多联机空调,輸出到以欧州为主导的国外市场。而在同月内,美的集团公布与开利集团公司在国外销售市场合资企业协作基本上,进一步加强在商用中央空调行业协作。 权威专家表明,中国公司在未来两年内国际性企业并购的脚步变的越来越快,尤其是家电业,预估更快三年,中国很有可能会问世家用电器情况的国际性大佬。 跨国并购风潮来临 上年至今,中国公司跨国并购加快,依据Dealogic的数据统计显示信息,截止2020年5月10日,中国公司跨国并购额度已达1110亿美金,超过上年全年度的1080亿美金,而同期相比企业并购额度则为750亿美金。 现阶段,中国有着极大的GDP、极大的销售市场、充裕的资产,可是全部产业生态展现中低档产业链比较严重产能过剩、中高档产业链欠缺决策权和主动权的难题。全世界企业并购是以供给侧结构项目投资、企业并购资本主义国家的高品质公司,随后根据融合使中国公司和资产得到高档产业链資源的一种最优化挑选。 伴随着大佬们“出航”脚步的加速,中国加工制造业有希望逐渐进到以自主创新与转型为核心的“智能制造时期”。 来源于:CPRJ 中国塑胶硫化橡胶 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
抱歉!该牌号暂无认证数据。
抱歉!暂无数据。
抱歉!暂无数据。