牌号简介 About |
---|
该UL 94 V-0级片材由回收树脂挤压而成,具有优异的抗冲击性、耐磨性和经济性,适用于一般用途的热成型和制造应用Boltaron 1165/1165C是一种专有的阻燃PVC/丙烯酸片材,其价格比具有竞争力的一般用途防火片材更优惠。采用精选树脂挤出,并对高性能螺栓片材进行修整和再研磨。因此,它表现出满足或超过许多一般热成型和制造要求的质量,例如10 ft.lbs./in的Izod冲击阻力。(530 J/m),具有广泛的耐化学性、极强的耐磨性和UL 94 V-0防火等级,同时降低了成本。提供六种表面纹理的黑色和深灰色,板材长度为120英寸。(3048毫米),宽度为60英寸。(1524毫米),厚度从.040到.250英寸。(1.02至6.35 mm)和定制毛坯尺寸。Boltaron 1165/1165C易于热成型,在深凹处和尖锐的外角产生均匀的壁厚。它也很容易被锯,钻孔,攻丝,走线和其他机械加工使用常规工具,可以刹车形成(更薄的仪表),热焊接,粘合和机械紧固,允许快速制造广泛的高完整性零件和总成。 Extruded from recycled resin, this UL 94 V-0 rated sheet offers excellent impact resistance, abrasion resistance and economy for general purpose thermoforming and fabricating applications Boltaron 1165/1165C is a proprietary, fire retardant PVC/Acrylic sheet that is favorably priced against competitive general purpose, fire rated sheet. It is extruded using select resin, trim and regrind of high performance Boltaron sheet. As a result, it exhibits qualities that meet or exceed many general thermoforming and fabrication requirements, such as Izod impact resistance of 10 ft. lbs./in. (530 J/m), broad chemical resistance, extreme abrasion resistance and a UL 94 V-0 fire rating, while reducing cost. Offered in black and dark gray colors in six surface textures, the sheet is offered in lengths to 120 in. (3048 mm), widths to 60 in. (1524 mm), thicknesses from .040 to .250 in. (1.02 to 6.35 mm) and in custom blank sizes. Boltaron 1165/1165C is readily thermoformed, yielding uniform wall thickness in deep recesses and sharp outside corners. It is also readily sawn, drilled, tapped, routed and otherwise machined using conventional tools, and can be brake formed (thinner gauges), heat welded, adhesive bonded and mechanically fastened, allowing rapid fabrication of a broad range of high-integrity parts and assemblies. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.41 | g/cm³ | ASTM D792 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
530 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
71.1 | ℃ | ASTM D648 |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.20 mm 1.20 mm |
V-0 | UL 94 | |
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
成型温度 Forming temperature |
168 到 196 | ℃ | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
美高功能复合资料市场将达100亿美元 碳纤维将占据85%
2016-08-18 近日,美国弗里多尼亚集团(Freedonia Group)发布一份有关高性能复合材料的市场报告。报告指出,美国对高性能复合材料的需求将以每年5.3%的速度增长,到2020年美国高性能复合材料市场总额将达100亿美元。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |