牌号简介 About |
---|
TRIEL® 5752SP是一种热塑性聚酯弹性体 (TPEE)产品,。 它,在亚太地区、北美洲或欧洲有供货。 TRIEL® 5752SP is a Thermoplastic Polyester Elastomer (TPEE) product. It is available in Asia Pacific, Europe, or North America. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.27 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
4.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
1.7 to 2.0 | % | ASTM D955 |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
0.50 | % | ASTM D570 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
75 | ASTM D2240 | |
拉伸强度 tensile strength |
ASTM D638 | ||
断裂 fracture |
MPa | ASTM D638 | |
5% 应变 5% strain |
MPa | ASTM D638 | |
10% 应变 10% strain |
MPa | ASTM D638 | |
50% 应变 50% strain |
MPa | ASTM D638 | |
拉伸应变 Tensile strain |
|||
断裂 fracture |
% | ASTM D638 | |
弯曲模量 Bending modulus |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
屈服 yield |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ASTM D256 | ||
-40℃ -40℃ |
J/m | ASTM D256 | |
23℃ 23℃ |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ASTM D648 | |
维卡软化温度 Vicat Softening Temp |
℃ | ASTM D1525 2 | |
熔融温度 Melting temperature |
℃ | ASTM D2117 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 标准 B (120°C/h), 压 力1 (10N) |
【新闻资讯】查看全部
3D打印行业困难 企业失败前似乎都很成功
2016-04-26 3D打印行业可以说是一个十分艰难的行业,不管公司的规模是大还是小,都会有时候一招不慎,犯下大错。在外部人看来,有时很难理解他们是如何失败的,而这些失败来临之前他们似乎都非常成功。 话说“失败是成功之母”,成功之路本就不是一条直线,本期我们一起来探讨这些公司的起起落落,我们通过透析因果关系来更清晰的理解3D打印行业的商业模式和扩张之路。 故事1:Maker Bot的过山车 一直以来,Maker Bot以一种看似不可阻挡的增长之势成为3D打印行业 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |