牌号简介 About |
---|
“MOPLEN”RP325M是一种控制流变性的轻微丙烯无规共聚物,用于生产高透明的铸造薄膜。该产品含有防滑剂和防堵剂。它具有很好的光学性能和良好的热焊接性。主要应用于糖果、面食、饼干和零食等食品的包装,书籍、文具、毛毯、衬衫和丝袜的包装。”MOPLEN“RP325M适用于食品接触。有关监管信息,请参阅“MOPLEN”RP325M产品管理公告(PSB)。 "Moplen" RP325M is a controlled rheology slightly propylene random copolymer for manufacturing high transparent cast films. The product contains slip- and antiblock agents. It exhibits very good optical properties and good heat weldability. Main applications are packaging of foodstuffs such as sweets, pasta, biscuits and snacks, packaging of books, stationary, blankets, shirts and hosiery. "Moplen" RP325M is suitable for food contact. For regulatory information please refer to "Moplen" RP325M Product Stewardship Bulletin ( PSB ). |
产品描述 Product Description
厂家:荷兰利安德巴塞尔 LyondellBasell
类别:PP共聚 PP copolymer
用途:包装;食品包装;流延薄膜;文具;
颜色:清晰/透明
加工条件:流延薄膜
性能特点: 抗结块性; 可控流变; 高光滑性; 透光性好; 无规共聚物; 食品接触; 光学性能; Good Clarity,Smoothness,Optical performance,Controllable rheological,High anti-blocking,Food contact compliance,Random copolymer
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
8.0 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
900 | MPa | ISO 527-1-2 |
拉伸强度 tensile strength |
|||
屈服 yield |
25.0 | MPa | ISO 527-2/50 |
拉伸应变 Tensile strain |
|||
屈服 yield |
11 | % | ISO 527-2/50 |
摩擦系数 friction coefficient |
ASTM D1894 | ||
与自身 - 动态 With oneself - dynamic |
ASTM D1894 | ||
与自身 - 静态 With oneself - static |
ASTM D1894 | ||
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
割线模量 Secant modulus 2 |
|||
MD,50 µm MD,50 µm 2 |
MPa | ASTM D882 | |
拉伸强度 tensile strength 3 |
ASTM D882 | ||
MD,屈服,50 µm MD, yield, 50 µ m |
MPa | ASTM D882 | |
MD,断裂,50 µm MD, fracture, 50 µ m |
MPa | ASTM D882 | |
拉伸应变 Tensile strain 3 |
ASTM D882 | ||
MD,屈服,50 µm MD, yield, 50 µ m |
% | ASTM D882 | |
MD,断裂,50 µm MD, fracture, 50 µ m |
% | ASTM D882 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
0℃ 0℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
A50 A50 |
℃ | ISO 306/A50 | |
光学性能 optical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
光泽度 gloss |
|||
45°,50 µm 45°,50 µm |
ASTM D2457 | ||
雾度 Haze |
|||
50 µm 50 µm |
% | ASTM D1003 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 1.2 in/min |
3 20 in/min |
【新闻资讯】查看全部
在美国的要求下 日本决定首次释放国家储备石油
2021-11-24 搜料网资讯: 据日本放送协会(NHK)24日报道,鉴于原油价格持续上涨,日本政府已经决定,将接受美国政府的要求,首次释放国家储备石油。 鉴于原油价格持续上涨,日本政府已经决 |
在美国的要求下 日本决定首次释放国家储备石油 搜料网资讯:据日本放送协会(NHK)24日报道,鉴于原油价格持续上涨,日本政府已经决定,将接受美国政府的要求,首次释放国家储备石油。
鉴于原油价格持续上涨,日本政府已经决定,将接受美国政府的要求,首次释放国家储备石油。图片来源:日本放送协会(NHK)报道截图 据报道,截至9月末,日本的国家石油储备量可满足145天的国内消费需求。目前,日本政府暂定将释放“数天”的量,是否追加释放仍在讨论中。 日本法律规定,释放储备石油只能在汽油供给不足或发生自然灾害时进行。不过,由于日本国内石油需求减少,日本政府判断,将多余部分放出不会违反法律。 据介绍,日本上一次“放油”还是在2011年6月,当时,受利比亚局势恶化影响,日本释放了部分民间储备,但释放国家储备还是尚属首次。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。