牌号简介 About |
---|
Sarlink TPV 4100系列是专为要求苛刻的汽车和工业应用而设计的工程材料。sarlink 4139D是一种低密度、高硬度的热塑性硫化胶,具有优异的拉伸强度、优异的压缩永久变形、耐化学性和高温性能。这一等级可以通过注射成型,吹塑和挤出应用,如密封,垫圈,耐化学性软管和管,靴子和波纹管。 SARLINK® TPV 4100 series are engineered materials designed primarily for demanding automotive and industrial applications. Available in both black and natural, SARLINK® 4139D is a low density, high hardness thermoplastic vulcanizate that exhibits exceptional tensile strength, superior compression set, chemical resistance and high temperature performance. This grade can be processed by injection molding, blow molding and extrusion for applications such as seals, gaskets, chemical resistant hose and tube, boots and bellows. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.948 | g/cm³ | ASTM D792 |
密度 Density |
0.950 | g/cm³ | ISO 1183 |
弹性体 elastic body |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
ASTM D412 | ||
TD,100% 应变 TD, 100% strain |
8.89 | MPa | ASTM D412 |
MD,100% 应变 MD, 100% strain |
13.3 | MPa | ASTM D412 |
拉伸强度 tensile strength |
ISO 37 | ||
TD,100% 应变 TD, 100% strain |
8.90 | MPa | ISO 37 |
MD,100% 应变 MD, 100% strain |
MPa | ISO 37 | |
拉伸强度 tensile strength |
ASTM D412 | ||
断裂 fracture |
MPa | ASTM D412 | |
MD,断裂 MD, fracture |
MPa | ASTM D412 | |
拉伸强度 tensile strength |
ISO 37 | ||
断裂 fracture |
MPa | ISO 37 | |
MD,断裂 MD, fracture |
MPa | ISO 37 | |
拉伸应变 Tensile strain |
ASTM D412 | ||
断裂 fracture |
% | ASTM D412 | |
流量,断裂 Flow rate, fracture |
% | ASTM D412 | |
拉伸应变 Tensile strain |
ISO 37 | ||
断裂 fracture |
% | ISO 37 | |
流量,断裂 Flow rate, fracture |
% | ISO 37 | |
撕裂强度 tear strength 2 |
|||
TD TD |
kN/m | ASTM D624 | |
MD MD 2 |
kN/m | ISO 34-1 | |
压缩形变 Compression deformation |
ASTM D395 | ||
23℃,22 hr 23℃,22 hr |
% | ASTM D395 | |
70℃,22 hr 70℃,22 hr |
% | ASTM D395 | |
125℃,70 hr 125℃,70 hr |
% | ASTM D395 | |
压缩形变 Compression deformation |
ISO 815 | ||
23℃,22 hr 23℃,22 hr |
% | ISO 815 | |
70℃,22 hr 70℃,22 hr |
% | ISO 815 | |
125℃,70 hr 125℃,70 hr |
% | ISO 815 | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
ASTM D2240 | ||
邵氏 D,5 秒,挤出成型 Shore D, 5 seconds, extrusion molding |
ASTM D2240 | ||
邵氏 D,5 秒,注塑成型 Shore D, 5 seconds, injection molding |
ASTM D2240 | ||
邵氏硬度 Shore hardness |
ISO 868 | ||
邵氏 D,5 秒,挤出成型 Shore D, 5 seconds, extrusion molding |
ISO 868 | ||
邵氏 D,5 秒,注塑成型 Shore D, 5 seconds, injection molding |
ISO 868 | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
相对温度指数 Relative temperature index |
|||
电气性能 Electrical performance |
℃ | UL 746 | |
强度机械性能 Strength mechanical performance |
℃ | UL 746 | |
冲击机械性能 Impact mechanical performance |
℃ | UL 746 | |
老化性能 Aging performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
ASTM D573 | ||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
100% 应变,135℃,1000 hr 100% strain, 135 ℃, 1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
100% 应变,150℃,168 hr 100% strain, 150 ℃, 168 hr |
% | ASTM D573 | |
空气中拉伸强度的变化率 - TD Change rate of tensile strength in air - TD |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
100% 应变 135℃,1000 hr 100% strain 135 ℃, 1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
100% 应变 150℃,168 hr 100% strain 150 ℃, 168 hr |
% | ISO 188 | |
空气中极限伸长率的变化率 - TD Change rate of ultimate elongation in air - TD |
ASTM D573 | ||
135℃,1000 hr 135℃,1000 hr |
% | ASTM D573 | |
150℃,168 hr 150℃,168 hr |
% | ASTM D573 | |
在空气中断裂时拉伸应力变化 - TD Changes in tensile stress when fractured in air - TD |
ISO 188 | ||
135℃,1000 hr 135℃,1000 hr |
% | ISO 188 | |
150℃,168 hr 150℃,168 hr |
% | ISO 188 | |
空气中硬度计硬度的变化率 The rate of change in hardness of a hardness tester in the air |
ASTM D573 | ||
邵氏 D,135℃,1000 hr Shaw's D, 135 ℃, 1000 hr |
ASTM D573 | ||
邵氏 D,150℃,168 hr Shore D, 150 ℃, 168 hr |
ASTM D573 | ||
空气中邵氏硬度的变化率 The rate of change of Shore hardness in air |
ISO 188 | ||
邵氏 D,135℃,1000 hr Shaw's D, 135 ℃, 1000 hr |
ISO 188 | ||
邵氏 D,150℃,168 hr Shore D, 150 ℃, 168 hr |
ISO 188 | ||
体积变化 Volume change |
|||
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ASTM D471 | |
125℃,70 hr,在IRM 903油中 125 ℃, 70 hr, in IRM 903 oil |
% | ISO 1817 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
1.00 mm,所有颜色 1.00 mm, all colors |
UL 94 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
熔体表观粘度 - Capillary,@ 206/s Apparent viscosity of melt - Capillary, @ 206/s |
|||
200℃ 200℃ |
Pa·s | ISO 11443 | |
200℃ 200℃ |
Pa·s | ASTM D3835 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 B 方法,直角形试样(不割口) |
【新闻资讯】查看全部
联合开发!路博润和ColorFabb联合开发3D打印材料varioShore TPU
2022-12-06 扫描上图二维码,可以免费下载 搜料 APP 路博润3D打印解决方案和总部位于荷兰的3D打印材料公司ColorFabb展示了联合开发的新型varioShore TPU材料。该联合开发旨在提高发泡能力,并为增材 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |