牌号简介 About |
---|
澳大利亚Lyondellbasell公司的聚丙烯级HP555E是一种具有常规分子量分布的低流量均聚物,其配方中添加了增强的工艺稳定性添加剂包。HP555E是为要求高熔体强度和熔体稳定性的挤出工艺而设计的。通常由HP555E制成的最终用途产品包括捆扎带、机械纤维纱线、型材和吹塑包装。 LyondellBasell Australia's Polypropylene grade HP555E is a very low flow homopolymer with a conventional molecular weight distribution and is formulated with an enhanced process stability additive package. HP555E is designed for extrusion processes which demand high melt strength and melt stability characteristics. End use products typically made from HP555E include strapping, mechanically fibrillated yarns, profiles and blow moulded packaging. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.900 | g/cm³ | ISO 1183/D |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
0.80 | g/10min | ISO 1133 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
23℃ 23℃ |
6.5 | kJ/m² | ISO 180-1A |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
82.0 | ℃ | ISO 75-2/B |
1.8 MPa,未退火 1.8 MPa, unannealed |
51.0 | ℃ | ISO 75-2/A |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
邵氏硬度 Shore hardness |
|||
邵氏 D Shaw's D |
ISO 868 | ||
拉伸强度 tensile strength |
|||
屈服 yield |
MPa | ISO 527-2 | |
弯曲模量 Bending modulus |
MPa | ISO 178 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
诺信在K展推出用于塑化螺杆的新型涂层技术
2016-10-08 一项使用极其微小的、仅仅比香烟烟雾中的颗粒大一点的碳化钨球技术,已经被用于生产适用于单、双塑化螺杆的涂层。据称,其耐磨性和耐腐蚀性均优于通过高速氧燃料 (HVOF) 热喷涂形成的标准涂层。诺信公司(Nordson)将在K 2016上推出这项技术。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |