NYCOA 534 H是一种高粘度、热稳定的有核尼龙6树脂。高粘度和快速安装时间使管材,棒,片材和薄膜的挤出成为一种优良的材料。由于其快速设置时间,快速挤出生产线的速度有B NYCOA 534小时是适用于需要连续暴露在温度超过110°C的应用。 NYCOA 534 H is a high viscosity; heat stabilized, nucleated Nylon 6 resin. The high viscosity and fast set-up time make an excellent material for extrusion of tubing, rods, sheet and film. Because of its fast set-up time, fast extrusion line speeds have b NYCOA 534 H is suitable for applications that require continuous exposure to temperatures in excess of 110° C. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.13 | g/cm³ | ASTM D792 |
吸水率 Water absorption rate |
|||
24hr 24hr |
1.8 | % | ASTM D570 |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
6.4mm 6.4mm |
59 | J/m | ASTM D256 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
ASTM D648 | ||
0.45 MPa,未退火 0.45 MPa, unannealed |
191 | ℃ | ASTM D648 |
1.8 MPa,未退火 1.8 MPa, unannealed |
65.6 | ℃ | ASTM D648 |
连续使用温度 Continuous use temperature |
℃ | ASTM D794 | |
熔融温度 Melting temperature |
℃ | DSC | |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
洛氏硬度 Rockwell hardness |
|||
R 级 R-level |
ASTM D785 | ||
拉伸强度 tensile strength 2 |
MPa | ASTM D638 | |
拉伸应变 Tensile strain 2 |
|||
断裂 fracture 2 |
% | ASTM D638 | |
弯曲模量 Bending modulus 2 |
MPa | ASTM D790 | |
弯曲强度 bending strength 2 |
MPa | ASTM D790 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 2.0 in/min |
【新闻资讯】查看全部
干货!PC注塑工艺的11个黄金技巧
2017-11-30 PC性能优异,透明度较高,冲击韧性好,耐蠕变,使用温度范围宽。 PC的工艺特性:熔融粘度对剪切率的敏感性小,而对温度的敏感性大,无明显熔点,熔融体粘度较高,高温下树脂易水解,制品易开裂。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |