牌号简介 About |
---|
ISPLEN® PP 084 Y1E是一种分子量分布窄的中高熔体流动速率聚丙烯均聚物,可在高速纤维(BCF/CF和SPUNBOND)生产线中进行最佳加工。它包括一种特殊配方,能够抵抗“气体褪色”着色,适用于在挤出过程和最终使用过程中保护聚合物。用于高速生产线中短纤维和BCF/CF挤压的典型应用。特别推荐用于纺粘线的工业非织造布。推荐的熔化温度范围为190至250°C。应优化每个生产线的加工条件。 ISPLEN® PP 084 Y1E is a medium-high melt flow rate polypropylene homopolymer with narrow molecular weight distribution which provides optimum processing in fibre lines of high speed (BCF/CF and spunbond). It includes a specific formulation resistant to "gas fading" coloration, suitable for protecting the polymer during extrusion process and final use. TYPICAL APPLICATIONS Indicated for the extrusion of staple fibre and BCF/CF in lines of high speed. Specially recommended for technical nonwovens in spunbond lines. Recommended melt temperature range from 190 to 250°C. Processing conditions should be optimised for each production line. |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
0.905 | g/cm³ | ISO 1183 |
熔体质量流动速率 Melt Flow Rate |
|||
230℃,2.16kg 230℃,2.16kg |
19 | g/10min | ISO 1133 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
屈服 yield |
36.0 | MPa | ISO 527-2 |
弯曲模量 Bending modulus |
1550 | MPa | ISO 178 |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
0.45 MPa,未退火 0.45 MPa, unannealed |
90.0 | ℃ | ISO 75-2/B |
维卡软化温度 Vicat Softening Temp |
℃ | ISO 306/A |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
淡季不淡 3月份国内动力煤以上涨为主
2021-05-01 搜料网资讯: [导语] 3月份国内动力煤市场再次出现淡季不淡的行情,主产地和北方港口煤价均维持高位水平运行。产地方面,以鄂尔多斯5500大卡动力煤为例,截至3月18日主流坑口含税 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |