牌号简介 About |
---|
开发中的产品是无筋聚酰胺66,中等粘度,用于注塑成型,带有特殊的结晶剂,用于快速循环。适用于食品接触应用 TECHNYL® A 221 Natural FA is an unfilled polyamide 66, for injection moulding, with a special crystallizing agent, for fast cycles. This grade offers a good combination between primary properties of the unreinforced polyamide 66 and processing properties leading to increased productivity. These performances are associated with excellent dimensional stability and good rigidity of moulded parts. It is designed to be used in food contact applications. |
产品描述 Product Description
厂家:德国道默 DOMO
类别:PA66 PA66
用途:阀门/阀门部件;电气/电子应用领域;汽车领域的应用;连接器;消费品应用领域;
颜色:自然色
加工条件:注射成型 Injection Molding
性能特点: 成核的; 成型周期快; 防火阻燃等级V-2; 食品接触; Food contact compliance,Nucleation,V-2,Quick molding cycle
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.14 | g/cm³ | ISO 1183/A |
吸水率 Water absorption rate |
|||
23℃,24hr 23℃,24hr |
1.1 | % | ISO 62 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
3200 | MPa | ISO 527-2/1A |
拉伸强度 tensile strength |
|||
屈服,23℃ Yield, 23 ℃ |
95.0 | MPa | ISO 527-2/1A |
屈服,23℃ Yield, 23 ℃ |
98.0 | MPa | ASTM D638 |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2 | |
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
弯曲模量 Bending modulus |
|||
23℃ 23℃ |
MPa | ISO 178 | |
23℃ 23℃ |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ |
MPa | ISO 178 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
|||
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
|||
23℃ 23℃ |
ISO 179/1eU | ||
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ASTM D648 | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/Af | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/Bf | |
熔融峰值温度 Melting peak temperature |
℃ | ASTM D3417 | |
熔融温度 Melting temperature |
℃ | ISO 11357-3 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
2 mm 2 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
IEC 60112 | ||
解决方案 A Solution A |
V | IEC 60112 | |
解决方案 B Solution B |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
0.80 mm 0.80 mm |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
1.6 mm 1.6 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index |
% | ISO 4589-2 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
德国公司消费微成型特弗龙零件
2017-02-23 德国慕尼黑的家族注塑企业Rohde & Schwarz,正使用来自威猛巴顿菲尔公司的注塑机生产微成型聚四氟乙烯部件。 这些部件之前是通过回转工艺进行生产的。 Rohde & |
德国公司消费微成型特弗龙零件 德国慕尼黑的家族注塑企业Rohde & Schwarz,正应用来源于威猛巴顿菲尔企业的注塑机生产制造微成形聚四氟乙烯构件。 这种构件以前是根据旋转加工工艺开展生产制造的。 Rohde & Schwarz创立于1933年,主要从事无线通讯层面的业务流程。该电子器件集团公司有着近10,000位职工,在精确测量技术性、广播节目和新闻媒体技术性、安全性通讯和互联网安全系数、无线电监测和无线通信精准定位技术性的业务流程行业内是一家全世界领跑企业。 该企业坐落于法国Teisnach的加工厂是从业机械设备和电子器件生产制造的系统供应商和研究中心。Rohde & Schwarz注塑生产加工高精密塑胶构件。 Rohde & Schwarz的全新微成形商品为供高频率零部件应用的聚四氟乙烯垫圈。该企业称,微成形比旋转加工工艺的成本费有显著优点。 来源于:塑料新闻我国 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
抱歉!暂无数据。
抱歉!暂无数据。