牌号简介 About |
---|
Durethan® BKV 15 G H2.0 900051 (干燥 ) PA 6-Copolymer, 15%玻璃纤维、注塑、热老化稳定,改善表面光洁度,天气稳定。 Durethan® BKV15GH2.0 900051 (Dry) PA 6, 15 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, weather stabilized Durethan® BKV15GH2.0 900051 PA 6, 15 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, weather stabilized Durethan® BKV15GH2.0 900051 PA 6, 15 % glass fibers, injection molding, heat-aging stabilized, improved surface finish, weather stabilized |
产品描述 Product Description
厂家:德国朗盛 LANXESS
类别:PA6 PA6
加工条件:注射成型 Injection Molding
性能特点: 防火阻燃等级HB; 热稳定性好; 共聚物; 耐候抗UV; 表面光泽度好; 耐老化; Weather resistance is good,Good heat aging resistance,Good surface appearance,Copolymer,Heat Stabilized,HB
填料:玻璃纤维 15
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.24 | g/cm³ | ISO 1183 |
表观密度 Apparent density |
0.70 | g/cm³ | ISO 60 |
收缩率 Shrinkage rate |
|||
TD:280℃,3.0 mm TD:280℃,3.0 mm 2 |
0.67 | % | ISO 2577 |
TD:120℃,3.0 mm,2 hrs TD:120℃,3.0 mm,2 hrs 3 |
0.21 | % | ISO 294-4 |
MD:280℃,3.0 mm MD:280℃,3.0 mm 2 |
0.34 | % | ISO 2577 |
MD:120℃,3.0 mm,2 hrs MD:120℃,3.0 mm,2 hrs 3 |
% | ISO 2577 | |
吸水率 Water absorption rate |
|||
饱和,23℃ Saturation, 23 ℃ |
% | ISO 62 | |
平衡,23℃,50% RH Equilibrium, 23 ℃, 50% RH |
% | ISO 62 | |
薄膜 film |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
膜刺穿强度 Membrane puncture strength |
ISO 6603-2 | ||
-- -- 6 |
J | ISO 6603-2 | |
-- -- 7 |
J | ISO 6603-2 | |
膜刺穿力 Membrane puncture force |
ISO 6603-2 | ||
-- -- 6 |
N | ISO 6603-2 | |
-- -- 7 |
N | ISO 6603-2 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
简支梁缺口冲击强度 Charpy Notched Impact Strength |
ISO 179/1eA | ||
-40℃ -40℃ |
kJ/m² | ISO 179/1eA | |
-30℃ -30℃ |
kJ/m² | ISO 179/1eA | |
23℃ 23℃ |
kJ/m² | ISO 179/1eA | |
简支梁无缺口冲击强度 Charpy Unnotch Impact strength |
ISO 179/1eU | ||
-30℃ -30℃ |
kJ/m² | ISO 179/1eU | |
23℃ 23℃ |
kJ/m² | ISO 179/1eU | |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
ISO 180/1A | ||
-40℃ -40℃ |
kJ/m² | ISO 180-1A | |
-30℃ -30℃ |
kJ/m² | ISO 180-1A | |
悬臂梁无缺口冲击强度 Notched impact strength of cantilever beam |
ISO 180/1U | ||
-30℃ -30℃ |
kJ/m² | ISO 180/1U | |
23℃ 23℃ |
kJ/m² | ISO 180/1U | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
8.0 MPa,未退火 8.0 MPa, unannealed |
℃ | ISO 75-2/C | |
1.8 MPa,未退火 1.8 MPa, unannealed |
℃ | ISO 75-2/A | |
0.45 MPa,未退火 0.45 MPa, unannealed |
℃ | ISO 75-2/B | |
维卡软化温度 Vicat Softening Temp |
|||
B50 B50 |
℃ | ISO 306 | |
B120 B120 |
℃ | ISO 306/B120 | |
熔融温度 Melting temperature 5 |
℃ | ISO 11357-3 | |
线性热膨胀系数 Linear coefficient of thermal expansion |
|||
TD:23~55℃ TD:23~55℃ |
1/℃ | ISO 11359-2 | |
MD:23~55℃ MD:23~55℃ |
1/℃ | ISO 11359-2 | |
电气性能 Electrical performance |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
表面电阻率 Surface resistivity |
ohms | IEC 60093 | |
体积电阻率 Volume resistivity |
|||
23℃ 23℃ |
ohms·cm | IEC 60093 | |
介电强度 Dielectric strength |
|||
23 ℃,1 mm 23 ℃,1 mm |
kV/mm | IEC 60243-1 | |
相对电容率 Relative permittivity |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
耗散因数 Dissipation factor |
IEC 60250 | ||
23℃,100 Hz 23℃,100 Hz |
IEC 60250 | ||
23℃,1 MHz 23℃,1 MHz |
IEC 60250 | ||
相比漏电起痕指数 Compared to the leakage tracing index |
|||
解决方案 A Solution A |
V | IEC 60112 | |
阻燃性能 FLAME CHARACTERISTICS |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
阻燃等级 Flame retardant level |
UL 94 | ||
1.60 mm 1.60 mm |
UL 94 | ||
3.20 mm 3.20 mm |
UL 94 | ||
灼热丝可燃性指数 Glowing wire flammability index |
|||
2.0 mm 2.0 mm |
℃ | IEC 60695-2-12 | |
极限氧指数 Extreme oxygen index 9 |
% | ISO 4589-2 | |
阻燃等级 Flame retardant level 10 |
ISO 3795 | ||
补充信息 Supplementary information |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
ISO Shortname ISO Shortname |
ISO 1874 | ||
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸模量 Tensile modulus |
|||
23℃ 23℃ |
MPa | ASTM D638 | |
23℃ 23℃ |
MPa | ISO 527-1-2 | |
拉伸强度 tensile strength |
|||
断裂,23℃ Fracture, 23 ℃ |
MPa | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
MPa | ISO 527-2/5 | |
拉伸应变 Tensile strain |
|||
断裂,23℃ Fracture, 23 ℃ |
% | ASTM D638 | |
断裂,23℃ Fracture, 23 ℃ |
% | ISO 527-2/5 | |
弯曲模量 Bending modulus 4 |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
23℃ 23℃ 4 |
MPa | ISO 178-A | |
弯曲强度 bending strength 4 |
|||
23℃ 23℃ |
MPa | ASTM D790 | |
3.50% 应变 3.50% strain |
MPa | ISO 178-A | |
23℃ 23℃ |
MPa | ISO 178 | |
弯曲应变 Bending strain 5 |
% | ||
球压硬度 Ball hardness |
MPa | ISO 2039-1 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
2 150x150x3; MT 80°C; 500 Bar |
3 150x105x3mm, 80°C MT, 500 bar |
4 150x150x3 |
5 150x105x3mm |
6 0.079 in/min |
7 Pull Rate: 2 mm/min; 50% RH |
8 2 mm/min |
9 -30°C |
10 23°C |
11 10°C/min |
12 程序 A |
13 US-FMVSS302 |
【新闻资讯】查看全部
广州石化环保工作获广东省生态环境厅肯定
2021-03-23 搜料网资讯: 近日,广州石化收到广东省生态环境厅感谢信,感谢广州石化十三五期间持续推进挥发性有机物治理,促进挥发性有机物和氮氧化物协同减排,为广东省打赢大气污染物防 |
广州石化环保工作获广东省生态环境厅肯定 搜料网资讯:近日,广州石化收到广东省生态环境厅感谢信,感谢广州石化“十三五”期间持续推进挥发性有机物治理,促进挥发性有机物和氮氧化物协同减排,为广东省打赢大气污染物防治攻坚战作出巨大贡献。 为响应中央要求、落实集团公司部署,“十三五”期间,广州石化制定并实施了《污染防治攻坚战三年实施方案》,方案包含蓝天保卫战、碧水保卫战、净土保卫战、提高环境监测监控能力等方面项目59个,总投资8.26亿元。 截至2020年10月30日,59个项目全部完成,建成了一批具有国内先进水平的安全环保设施,有效提升广州石化安全环保水平。 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |
价格走势图
开始时间:
结束时间:
材料厂家:
【牌号齐全,内容全面】
全网共2500+项牌号+上游原料单体+原油价格,最长可追溯近20年价格行情
【精准,及时,权威!】
专业团队挖掘行情信息,第一时间发布行情
抱歉!该牌号暂无认证数据。
免责声明:参考价格是搜料网根据网络大数据拟合分析的结果,仅供参考。实际成交价取决但不限于以下因素:下单时间,付款方式,交货方式,数量,税费,色号,产地,项目信息。
- 电动汽车零件壳体的轻量化
- 2022-07-20 0
- Durethan® BKV 50 H3.0 000000 含有50%的玻璃纤维增强的PA 6材料,用注射成型的方式进行加工,具有良好的热老化稳定性。
- 阅读全文
电动汽车零件壳体的轻量化
1-符合冷却系统方面的要求
2-满足轻量化需求
3-拥有良好的强度与刚度
4-对冷却剂有更好的耐受性
5-优异的耐热性,能长期承受85℃的温度
6-热稳定性好
7-对水乙二醇混合物的长期耐受性好
8-爆破载荷高达10bar
2-满足轻量化需求
3-拥有良好的强度与刚度
4-对冷却剂有更好的耐受性
5-优异的耐热性,能长期承受85℃的温度
6-热稳定性好
7-对水乙二醇混合物的长期耐受性好
8-爆破载荷高达10bar
收起
抱歉!暂无数据。