牌号简介 About |
---|
PRL TP-FRHG30是一种聚丁烯对苯二甲酸酯(PBT)产品,含有的填充物为30% 玻璃纤维增强材料。 它可以通过注射成型进行加工, 特性包括: 通过 ROHS 认证 Flame Retardant 美观 耐热 PRL TP-FRHG30 is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include: RoHS Compliant Flame Retardant Good Aesthetics Heat Resistant |
技术参数 Technical Data | |||
---|---|---|---|
物理性能 PHYSICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
密度 Density |
1.65 | g/cm³ | ASTM D792 |
熔体质量流动速率 Melt Flow Rate |
|||
250℃,2.16kg 250℃,2.16kg |
1.0 to 5.0 | g/10min | ASTM D1238 |
收缩率 Shrinkage rate |
|||
MD MD |
0.30 to 0.90 | % | ASTM D955 |
机械性能 MECHANICAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
拉伸强度 tensile strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
117 | MPa | ASTM D638 |
屈服,3.17 mm Yield, 3.17 mm |
117 | MPa | ASTM D638 |
弯曲模量 Bending modulus |
|||
3.17 mm 3.17 mm |
MPa | ASTM D790 | |
弯曲强度 bending strength |
|||
断裂,3.18 mm Fracture, 3.18 mm |
MPa | ASTM D790 | |
冲击性能 IMPACT |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
悬臂梁缺口冲击强度 Impact strength of cantilever beam notch |
|||
3.2mm 3.2mm |
J/m | ASTM D256 | |
热性能 THERMAL |
额定值 Nominal Value |
单位 Units |
测试方法 Test Method |
热变形温度 Hot deformation temperature |
|||
1.8 MPa,未退火,3.2 mm 1.8 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 | |
0.45 MPa,未退火,3.2 mm 0.45 MPa, unannealed, 3.2 mm |
℃ | ASTM D648 |
备注 |
---|
1 一般属性:这些不能被视为规格。 |
【新闻资讯】查看全部
供需压力改善,化工原料PX完成7连涨
2017-11-10 10月27日至11月7日,亚洲化工原料PX价格实现7连涨,累计上涨了61.5美元/吨,目前已经成功突破900美元/吨CFR中国关口。成本端原油在超供格局好转预期下强势攀升、中国PTA工厂需求目前已经开始缓慢复苏,而消息面利好因素也在逐渐增多,市场整体气氛趋于向暖,也在进一步助推了PX价格走势上扬。 成本端油市利多氛围较为明显:其一,因为地缘冲突因素加剧了市场担忧气氛,沙 |
【免责声明】 广州搜料信息技术有限公司保留所有权利。 此数据表中的信息由搜料网soliao.com从该材料的生产商处获得。搜料网soliao.com尽最大努力确保此数据的准确性。 但是搜料公司对这些数据值及建议等给用户带来的不确定因素和后果不承担任何责任,并强烈建议在最终选择材料前,就数据值与材料供应商进行验证。 |